在较高浓度的AgNO3溶液中,采用聚乙烯吡咯烷酮(PVP)为保护剂,次磷酸钠(NaH2PO2·H2O)为还原剂,通过化学还原法成功制备出纳米银粉.采用设计3因素3水平的正交实验L9(33),考察了还原剂浓度、保护剂用量及反应温度对纳米银粉粒度及形貌的影响,获得制备纳米银粉的最佳条件:在AgNO3浓度为1.0 mol/L时,NaH2PO2·H2O浓度为0.1 mol/L,PVP,AgNO3(质量比)为1:1,溶液pH值为1～2,反应温度为40℃的条件下,制备出类球形、分散均匀、纯度高的纳米银粉,其粒度主要分布在30～50 nm范围.
参考文献
| [1] | Saito N.;Sato K.;Inoue Y.;Nishiyama H. .Artificial control of reaction selectivity on Ag metal surface by dynamic lattice displacement of acoustic waves[J].Surface Science: A Journal Devoted to the Physics and Chemistry of Interfaces,2000(0):1099-1103. |
| [2] | Xu XY;Yang QB;Wang YZ;Yu HJ;Chen XS;Jing XB .Biodegradable electrospun poly(L-lactide) fibers containing antibacterial silver nanoparticles[J].European Polymer Journal,2006(9):2081-2087. |
| [3] | Chau J L H;Hsu M K;Hsieh C C et al.[J].Materials Letters,2005,59:905. |
| [4] | Paszti Z;Peto G;Horvath Z E et al.[J].Nuclear Instruments and Methods in Physics Research,2001,178:131. |
| [5] | Chou KS.;Ren CY. .Synthesis of nanosized silver particles by chemical reduction method[J].Materials Chemistry and Physics,2000(3):241-246. |
| [6] | 廖立,熊继,谢克难.液相还原法制备纳米银粉的研究[J].稀有金属材料与工程,2004(05):558-560. |
| [7] | 孙红刚,刘恒,尹光福,刘卫,栾亚兰,余艳丽.纳米银溶胶的固液分离研究[J].稀有金属材料与工程,2006(07):1146-1149. |
| [8] | 宋永辉,梁工英,张秋利,卢学刚,魏春阳.球形纳米银粉的制备研究[J].稀有金属材料与工程,2007(04):709-712. |
| [9] | 印万忠,李先学,韩跃新,王泽红,梁军,赖茂明.液相化学还原法制备纳米银粉[J].矿冶,2003(04):48-50,43. |
| [10] | 张宗涛;赵斌;胡黎明 et al.[J].华东理工大学学报(自然科学版),1995,21(04):423. |
| [11] | 固大明;孙沫莹 .[J].哈尔滨工业大学学报,2003,35(08):1009. |
| [12] | 大连理工大学无机化学教研室.无机化学[M].北京:高等教育出版社,2001:202. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%