用Brabender扭矩塑化仪、HAAKE毛细管流变仪和吹膜机考察了硬脂酸镧与三硬脂酸甘油酯等组成的混和型配合物(LaC)对线型低密度聚乙烯(LLDPE)加工性能的影响.与纯LLDPE相比,加入5%(质量)LaC的体系,在密炼过程最大扭矩减小20.1%,平衡扭矩减小12.5%,塑化能降低17.1%;含该复合物0.25%(质量)的LLDPE仍为假塑性流体,与未含LaC的体系相比,毛细管挤出过程中表观粘度明显降低,非牛顿指数略有增大,在相同剪切速率下粘流活化能轻微减小;相同条件下吹膜时,加入0.25%该复合物,可使主机电流降低达9.2%,又吹膜工艺性能及外观明显改善,对薄膜的力学性能无不良影响.LaC是一种有效的LLDPE加工改性剂.
参考文献
| [1] | Colwell R .[J].Plastics Technology,1985,31(08):81-82. |
| [2] | Tzoganakis C;Price B C;Haizikiriakos S G .[J].Journal of Rheumatology,1993,37(02):355-365. |
| [3] | Hatzikiriakos S G .[J].Polymer Engineering and Science,1994,34(19):1441-1449. |
| [4] | Richard C G;Edwin P D .[P].WO 9105009,1991. |
| [5] | Duchesne D E;Johnon B V .[P].US Patent,U.S.5015693,1991. |
| [6] | Metzler R B;Foster G N .[P].US 4535113,1985. |
| [7] | 冯嘉春,黄志镗,陈鸣才.硬脂酸镧复合物对聚丙烯β晶型的诱导作用[J].高等学校化学学报,2001(01):154-156. |
| [8] | Feng J C;Chen M C;Huang Z T .[J].Journal of Applied Polymer Science,2001,82(06):1339-1345. |
| [9] | Nielsen L E.Polymer Rheology[M].New York and Basel: Marcel Dekker, Inc,1977:31-49. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%