以H2O-HCl-CaCl2溶液为反应介质采用两步法在常压下对脱硫石膏脱色;考察了HCl浓度、CaCl2浓度、料浆浓度对水热反应时间的影响和转晶温度、转晶时间、料浆浓度对产品白度和收率的影响.得出的较适宜条件为:HCl浓度为1.21 mol/L,CaCl2浓度为0.27 mol/L,料浆浓度为6.98％,转晶温度25 ℃、转晶时间18 h,该条件下水热反应时间缩短至120 min,脱色产品的白度和纯度分别提高至90％和96％.脱色提纯过程的母液反复利用5次后,产品性能与初次配料时无明显差异.以提纯脱色后的脱硫石膏为原料制备的半水硫酸钙晶须白度达到95.22％.
参考文献
| [1] | Chea Chandara;Khairun Azizi Mohd Azizli;Zainal Arifin Ahmad .Use of waste gypsum to replace natural gypsum as set retarders in portland cement[J].Waste Management,2009(5):1675-1679. |
| [2] | Halit Yazici .Utilization of coal combustion byproducts in building blocks[J].Fuel,2007(7/8):929-937. |
| [3] | C. Leiva;C. Garcia Arenas;L.F. Vilches .Use of FGD gypsum in fire resistant panels[J].Waste Management,2010(6):1123-1129. |
| [4] | 邓志银,袁义义,孙骏,史培阳,姜茂发.反应条件对脱硫石膏晶须生长行为的影响[J].矿产综合利用,2009(04):16-19. |
| [5] | Baohong Guan;Liuchun Yang;Zhongbiao Wu;Zhuoxian Shen;Xianfa Ma;Qingqing Ye .Preparation of α-calcium sulfate hemihydrate from FGD gypsum in K, Mg-containing concentrated CaCl_2 solution under mild conditions[J].Fuel,2009(7):1286-1293. |
| [6] | 曾学礼,胡银珍,楼文斌.脱硫石膏的物化特征及其综合利用[J].宁波工程学院学报,2012(02):67-72. |
| [7] | 崔益顺,刘勇,付凌杰,刘飞.石膏制备硫酸钙晶须工艺研究[J].四川理工学院学报：自然科学版,2012(01):38-40. |
| [8] | 徐锐,陈权,郭进武.烟气脱硫石膏溶液法制备α-半水石膏的工艺研究[J].化学与生物工程,2011(02):78-80. |
| [9] | Li ZB;Demopoulos GP .Development of an improved chemical model for the estimation of CaSO4 Solubilities in the HCl-CaCl2-H2O system up to 100 degrees C[J].Industrial & Engineering Chemistry Research,2006(9):2914-2922. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%