采用电火花沉积工艺,在铸钢表面制备了WC-4Co沉积涂层,采用X射线衍射仪、扫描电镜、显微硬度计等对沉积层的相结构、显微组织、显微硬度及耐磨性能进行了分析.结果表明:沉积层主要由Co3W3C、Fe3W3C、W2C、Fe7W6等相组成;沉积层与基体呈冶金结合,Fe7W6、W2C等硬质相弥散分布于沉积层中,部分区域硬质相达到了纳米颗粒尺寸;沉积层的平均硬度为1517HV0.3,约是基体硬度(502 HV0.3)的3倍;其耐磨性能比基体提高了2.4倍;沉积层的主要磨损机制为疲劳磨损,细小的弥散分布的硬质相是沉积层硬度以及耐磨性能提高的主要因素.
参考文献
| [1] | Jian-sheng Wang,Hui-min Meng,Hong-ying Yu,Zi-shuan Fan,Dong-bai Sun.Characterization and wear behavior of WC-0.8Co coating on cast steel rolls by electro-spark deposition[J].矿物冶金与材料学报,2009(06):707-713. |
| [2] | ZHANG Kun,何业东,WANG De-ren.电火花沉积MCrAlY涂层及其高温氧化行为[J].材料热处理学报,2008(04):143-147. |
| [3] | WANG Jiansheng,MENG Huimin,YU Hongying,FAN Zishuan,SUN Dongbai.Wear characteristics of spheroidal graphite roll WC-8Co coating produced by electro-spark deposition[J].稀有金属(英文版),2010(02):174-179. |
| [4] | 罗成,熊翔,董仕节,罗平.点焊电极表面电火花沉积TiB_2涂层的特征[J].材料热处理学报,2009(06):178-182. |
| [5] | Ribalko AV.;Sahin O. .The use of bipolar current pulses in electrospark alloying of metal surfaces[J].Surface & Coatings Technology,2003(2/3):129-135. |
| [6] | Frangini S.;Masci A.;Di Bartolomeo A. .Cr7C3-based cermet coating deposited on stainless steel by electrospark process: structural characteristics and corrosion behavior[J].Surface & Coatings Technology,2002(2/3):279-286. |
| [7] | 罗成,董仕节,熊翔.电火花振动沉积TiC功能涂层的显微组织与性能[J].材料热处理学报,2008(02):123-127. |
| [8] | 邵荷生;曲敬信;许小棣.摩擦与磨损[M].北京:煤炭工业出版社,1992 |
| [9] | 郑良桂.电火花表面强化工艺[M].北京:机械工业出版社,1987 |
| [10] | 王新林,石世宏,郑启光.激光熔覆层凝固特征与凝固组织控制研究[J].应用激光,2001(03):164-166. |
| [11] | 张文铖.焊接冶金学[M].北京:机械工业出版社,1995 |
| [12] | 乔生儒,韩栋,李玫.钢铁表面电火花淬火组织超细化及机理[J].机械工程材料,2004(08):7-9. |
| [13] | Wang R J;Qian Y Y;Liu J .Structural and interfacial analysis of WC92-Co8 coating deposited.titanium alloy by electrosparh deposition[J].Applied Surface Science,2004,228(04):405-409. |
| [14] | 梁秀兵,程江波,刘燕,白金元,徐滨士.铁基非晶纳米晶涂层的耐磨性研究[J].装甲兵工程学院学报,2009(05):77-81. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%