利用SEM和XRD对锈层的腐蚀形貌和腐蚀产物组成进行观察和分析，研究了N80裸钢和模拟全浸区腐蚀试样及模拟干湿交替腐蚀试样在两种海水介质中的极化行为。结果表明，干湿交替腐蚀阴极过程溶解氧还原的极限扩散控制特征基本消失，而受腐蚀产物还原为主的电荷传递控制。N80钢干湿交替腐蚀电流不仅包括钢自身的腐蚀电流，还包括腐蚀产物的氧化还原电流，导致了N80钢模拟干湿交替的腐蚀速率远大于全浸区腐蚀速率。
The polarization behavior of N80 steel was obtained from the corroded steel samples under wet-dry cyclic condition and compared with that from bare steel and immersion samples. The corrosion morphology and corrosion products of the steel samples were characterized using scanning electron microscopy (SEM) and X-ray diffraction (XRD). The cathodic reduction of samples under wet-dry cyclic condition was controlled mainly by the charge transfer step of reduction of corrosion products rather than the limiting diffusion control of dissolved oxygen. The matrix metal of the samples was corroded and the rust itself also took part in the reduction processes and hence increased the corrosion rate of the steel samples under wet-dry cyclic condition.
参考文献
| [1] | S. Syed .Atmospheric corrosion of hot and cold rolled carbon steel under field exposure in Saudi Arabia[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(6):1779-1784. |
| [2] | S. Rivero;B. Chico;D. de la Fuente .Corrosion atmosferica del acero bajo en carbono en un ambiente marino polar--Estudio del efecto del regimen de vientos[J].Revista de Metalurgia,2007(5):370-383. |
| [3] | G. Fajardo;P. Valdez;J. Pacheco .Corrosion Of Steel Rebar Embedded In Natural Pozzolan Based Mortars Exposed To Chlorides[J].Construction and Building Materials,2009(2):768-774. |
| [4] | Corrosion of vertical mild steel strips in seawater[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(10):2291. |
| [5] | 黄桂桥.合金元素对钢在海水飞溅区腐蚀的影响[J].腐蚀与防护,2001(12):511-513,516. |
| [6] | Khandaker M. Anwar Hossain;Said M. Easa;Mohamed Lachemi .Evaluation Of The Effect Of Marine Salts On Urban Built Infrastructure[J].Building and environment,2009(4):713-722. |
| [7] | 邵怀启,韩文礼,王雪莹,李爱贵.海洋飞溅区钢结构的腐蚀规律与防护措施[J].腐蚀与防护,2008(11):646-649. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%