研究了三元复相合金Cu-20Ni-30Cr(at%)在700℃和800℃纯氧气中的氧化行为.合金由三相组成,具有最大Cu浓度和最小Cr浓度的a相为合金的基体,中间浓度的Ni和Cr的β相和富Cr的y相以颗粒状态分布在合金基体中.合金在2个温度下的氧化动力学曲线偏离抛物线规律,其氧化增重随时间延长而降低,合金氧化速率随温度升高而加快.合金形成了复杂的氧化膜结构,外层为富Cu氧化物,中间层为尖晶石层,最内层为不规则但连续的Cr2O3膜.合金中的复相组织限制Cr在合金中的扩散,抑制了外氧化膜的形成.
参考文献
| [1] | SIMS C T;Stoloff;Hagel W C.Superalloys Ⅱ[M].New York:Academics Press,1987:153. |
| [2] | Kofstad P.High Temperature Corrosion[M].New York:Elsevier Applied Science,1988:389. |
| [3] | Wagner C.[J].Journal of the Electrochemical Society:369. |
| [4] | Gesmundo F;Niu Y .[J].Oxidation of Metals,1998,50(1-2):1. |
| [5] | Villars P;Prince A;Okamoto H.Hand Book of Ternary Alloy Phase Diagram[M].Ohio:ASM,1997:8734. |
| [6] | Cao Z Q;Niu Y;Gesmundo F .[J].Oxidation of Metals,2001,56(3-4):287. |
| [7] | Cao Z Q;Niu Y;Farne G.[J].High Temperature Materials and Processes,2001(5-6):377. |
| [8] | Cao Z Q;Gesmundo F;Al-Omary M et al.[J].Oxidation of Metals,2002,57(5-6):395. |
| [9] | Birk N;Richert H.[J].Journal of the Institute of Metals:308. |
| [10] | Niu Y;Gesmundo F;Wu W T .[J].Oxidation of Metals,1997,47(1-2):21. |
| [11] | Niu Y;Gesmundo F;Douglass D L et al.[J].Oxidation of Metals,1997,48(5-6):357. |
| [12] | Gesmundo F;Niu Y;Oquab D et al.[J].Oxidation of Metals,1998,49(1-2):115. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%