分析了我国核电承压设备（反应堆压力容器、主管道、蒸发器、稳压器和安全壳等）用钢的发展现状与发展方向,并指出某些元素在核电承压设备用钢中的作用及对其辐照脆化的影响。分析认为,为了确保核电承压设备用钢的使用性能和安全性能,必须严格控制残余元素水平、组织形态等,保证锻压比和后期退火工艺参数。
Recent development situation of steel plate used for nuclear pressure equipment（reactor pressure vessel,main pipe,evaporator,regulator,containment,etc.） in China,the effects of some alloying elements on the irradiation embrittlement of steel are described in this paper.In order to make sure that the performance and safety properties of the steel can satisfy the requirements of nuclear pressure equipment,it is necessary to control strictly the content of residual elements and steel microstructure.In addition,the forging ratio and post annealing process parameters are also needed to be guaranteed.
参考文献
| [1] | 李宏明.核电及核电用钢的发展[J].世界钢铁,2007(02):70-71. |
| [2] | 李云良,张汉谦,彭碧草,李金富.核电压力容器用钢的发展及研究现状[J].压力容器,2010(05):36-43. |
| [3] | 王发民,戴建中.民用核电反应堆压力容器制造要点[J].一重技术,2009(03):27-28. |
| [4] | 陈红字.核反应堆压力容器锻件用SA508系列钢的比较和分析[J].大型铸锻件,2009(01):243. |
| [5] | 杨文斗.反应堆材料学[M].北京:原子能出版社,2006 |
| [6] | 李颖,刘涛,栾培锋,史巨元.核电厂压水堆主管道材料性能的研究[J].物理测试,2006(05):12-13,18. |
| [7] | 薛飞,束国刚,余伟炜,遆文新,林磊,蒙新明,刘江南.核电厂主管道材料低周疲劳寿命预测方法评价[J].核动力工程,2010(01):23-27. |
| [8] | 董毅,高志远.我国核电事业的发展与Inconel 690合金的研制[J].特钢技术,2004(03):45-48. |
| [9] | 但体纯,王俭秋,韩恩厚,柯伟.压水堆核电站蒸汽发生器用600合金管在含铅高温碱溶液中的应力腐蚀行为研究[J].腐蚀科学与防护技术,2008(05):313-316. |
| [10] | 王珉 .16MND5稳压器锻件的工艺研究[J].核动力工程,1999,8:373-374. |
| [11] | 康大韬.大锻件材料及热处理[M].北京:龙门书局,1998 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%