制备了聚四氟乙烯(PTFE)、聚醚砜(PES)和聚偏氟乙烯(PVDF)作为支撑层材料的3种PDMS复合膜,研究了支撑层对复合膜分离水中乙酸性能的影响.结果表明,复合膜的分离性能不仅取决于活性层的物理化学性质,也与支撑层的结构及制备方法有关.随着料液浓度的增大,3种复合膜的渗透通量均增加,但分离因子却因不同支撑层材料而不同;随着料液温度的升高,3种复合膜的通量均大幅度增加,分离因子则随之下降;随着料液流速的增加,3种复合膜的渗透通量均先增加而后趋于平稳,分离因子则先降低而后几乎不变.
参考文献
| [1] | 徐冬梅,张可达,樊智虹,郑惠.组成对光固化聚氨酯与CPVC共混膜渗透汽化性能的影响[J].功能材料,2001(06):667-669. |
| [2] | S. Farooq;I.A. Karimi .Modeling support resistance in zeolite membranes[J].Journal of Membrane Science,2001(1):109-121. |
| [3] | F.Lipnizki;J.Olsson;A.Weis;G.Tragardh;R.W.Field .Hydrophobic pervaporation:influence of the support layer of composite membranes on the mass transfer[J].Separation Science and Technology,2002(8):1747-1770. |
| [4] | Vankelecom I.F.J.;Verschueren G.;Jacobs P.A.;Moermans B. .Intrusion of PDMS top layers in porous supports[J].Journal of Membrane Science,1999(1):289-297. |
| [5] | Trifunovic O;Tragardh G .The influence of support layer on mass transport of homologous series of alcohols and esters through composite pervaporation membranes[J].Journal of Membrane Science,2005(1/2):122-134. |
| [6] | Zhang L;Yu P;Luo YB .Comparative behavior of PVA/PAN and PVA/PES composite pervaporation membranes in the pervaporative dehydration of caprolactam[J].Journal of Applied Polymer Science,2007(6):4005-4011. |
| [7] | 刘丽,陈勇,李恕广,邓麦村.非对称复合膜支撑层阻力对水蒸气渗透影响的研究[J].膜科学与技术,2000(04):19-24. |
| [8] | 罗莹,李磊,王辉,谭淑娟,张志炳.支撑层结构对醇类渗透汽化过程的影响[J].化学工程,2008(05):44-47. |
| [9] | Mohammadi T;Aroujalian A;Bakhshi A .Pervaporation of dilute alcoholic mixtures using PDMS membrane[J].Chemical Engineering Science,2005(7):1875-1880. |
| [10] | Li L;Xiao Z Y;Tan S J et al.[J].Journal of Membrane Science,2004,243(1-2):177-187. |
| [11] | 刘铁勇 .渗透汽化法水中脱醇及传质过程的研究[D].北京化工大学,2007. |
| [12] | 江扬,韩德昌,魏民,魏健敏.聚偏氟乙烯膜结构的研究[J].天津纺织工学院学报,1996(03):6-11. |
| [13] | 李磊,谭淑娟,蒋冬华,武法文,徐志红,张志炳.支撑层对硅橡胶复合膜渗透汽化分离性能的影响[J].化工学报,2006(01):61-65. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%