A program on the solidification process of horizontal centrifugal casting coupled with eutectic carbides segregation has been developed in this paper. Due to the geometrical features of work roll, a cylindrical coordinate system was used. The temperature field of the outer layer at the end of filling process was imported as the initial temperature condition for the solidification process. The model of eutectic carbides segregation caused by different densities between eutectic MC and the molten steel was coupled in the program. The temperature field of the outer layer of work roll during horizontal centrifugal casting process was investigated. Results show that the outer layer has a "sandwich shape" solid fraction manner. Results also indicate that the segregation of eutectic MC is quite severe during centrifugal casting process. It forms four zones of different content of carbides in radial direction. The simulated results of MC carbides segregation phenomenon agree with the experimental observations.
参考文献
| [1] | L. Drenchev, J. Sobczak, S. Malinov and W. Sha: Model. Simul. Mater. Sci. Eng., 2003, 11, 635.[2 ] L. Drenchev, J. Sobczak, S. Malinov and W. Sha: Model. Simul. Mater. Sci. Eng., 2003, 11, 651.[3 ] C.G. Kang, P.K. Rohatgi, C.S. Narendranath and G.S. Cole: ISIJ Int., 1994, 34, 247.[4 ] D.Y. Ju and T. Inoue: J. Therm. Stresses, 1992, 15, 109.[5 ] J.W. Gao and C.Y. Wang: Mater. Sci. Eng. A, 2000, 292, 207.[6 ] H.G. Fu and J.H. Liu: Special Casting Nonferrous Alloys, 1995, 5, 31. (in Chinese)[7 ] D.Y. Ju, Y. Oshika and T. Inoue: Material, 1991, 40, 144. (in Japanese)[8 ] E.N. Souza, N. Cheung, C.A. Santos and A. Garcia: Inverse Probl. Sci. Eng., 2006, 14, 467.[9 ] Y. Ebisu: AFS Trans., 1977, 85, 85.[10] Z.A. Xu: Ph.D. Thesis, University of Ghen, 1993, 50.[11] Y.P. Minosyan, A.A. Ryadno, Y. Gsolov'yev and V.G. Gerasimov: Heat Transfer-Sov. Res., 1983, 15, 134.[12] H.G. Fu, Q. Xiao and J.D. Xing: Mater. Sci. Eng. A, 2008, 479, 253.[13] N.N. Song, Z.A. Xu, X.H. Kang, D.Z. Li and Y. Houbaert: in 3rd International Conference on Simulation and Modelling of Metallurgical Processes in Steelmaking, Leoben, Austria, 2009, SP2.[14] N.N. Song, Y.K. Luan, X.H. Kang, L.J. Xia and D.Z. Li: China Foundry, 2009, 6, 314.[15] K.C. Hwang, S. Lee and H.C. Lee: Mater. Sci. Eng. A, 1998, 254, 282.[16] K. Ichino, Y. Kataoka and T. Koseki: KAWASAKI Steel Technical Report (Japan), 1997, 37, 13. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%