采用销盘摩擦磨损试验机研究了不同载荷下45钢与DC53钢(Cr12MoV1)的干滑动摩擦学行为.通过SEM、XRD、SIMS等分析了45钢的磨损机理及其摩擦诱发的变形层特征.结果表明,载荷从40 N增加到60 N时,45钢销试样的磨损率增加量远大于DC53钢盘试样的磨损率增加量,载荷的变化对平均摩擦系数的大小几乎无影响;40 N载荷条件下,45钢销试样表面主要发生磨粒磨损和轻微的粘着磨损,60 N载荷条件下,45钢销试样表面主要发生粘着磨损;45钢销试样的摩擦影响层均由摩擦表层和塑性变形层组成,60 N载荷条件下销试样的塑性变形层深度大于40 N载荷条件下的销试样;45钢销试样的磨损表层出现了晶粒细化的现象,60 N载荷条件下的晶粒细化更明显;磨损表层中的细晶铁素体主要是由摩擦磨损过程中摩擦热和塑性变形共同作用导致的动态再结晶诱发的.
参考文献
| [1] | 薛群基.中国摩擦学研究和应用的重要进展[J].科技导报,2008(23):3. |
| [2] | 王军威,李国禄,王海斗,徐滨士,康嘉杰.氮碳共渗45钢的滚动接触疲劳失效机理[J].材料热处理学报,2012(10):124-129. |
| [3] | 刘莉莉,麦永津,揭晓华,于能,郑向新.45#钢表面纳米晶层的高温磨损特性[J].摩擦学学报,2010(03):285-290. |
| [4] | 王爱琴,谢敬佩,王文焱,李继文,李洛利.表面感应淬火对45钢滚动磨损特性的影响[J].材料热处理学报,2007(01):127-129. |
| [5] | 苏振国,安健,田旭,陆有,杨永利,孙世杰.稀土粉末渗硼45钢的磨损与腐蚀性能[J].材料热处理学报,2009(06):183-186,190. |
| [6] | Wang, L.;Zhou, J.;Liang, J.;Chen, J. .Microstructure and corrosion behavior of plasma electrolytic oxidation coated magnesium alloy pre-treated by laser surface melting[J].Surface & Coatings Technology,2012(13):3109-3115. |
| [7] | G. Sutter;N. Ranc .Flash temperature measurement during dry friction process at high sliding speed[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2010(11/12):1237-1242. |
| [8] | H.-J. Kim;A. Emge;R.E. Winter .Nanostructures generated by explosively driven friction: Experiments and molecular dynamics simulations[J].Acta materialia,2009(17):5270-5282. |
| [9] | Rigney D A .Comments on the sliding wear of metals[J].Tribology International,1997,30(5):361-367. |
| [10] | Mitjan Kalin .Influence of flash temperatures on the tribological behaviour in low-speed sliding: a review[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):390-397. |
| [11] | X. Meng-Burany;T. A. Perry;A. K. Sachdev;A. T. Alpas .Subsurface sliding wear damage characterization in Al-Si alloys using focused ion beam and cross-sectional TEM techniques[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2011(3/4):152-162. |
| [12] | Venkataraman B;Sundararajan G .The sliding wear behaviour of A1-SiC particulate composites.II.The characterization of subsurface deformation and correlation with wear behaviour[J].Acta Materialia,1996,44(2):461-473. |
| [13] | Lim S C;Ashby M F .Wear mechanism maps[J].Acta Materialia,1987,35(1):1-24. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%