超低碳钢连铸结晶器用保护渣研究现状

钢铁, 1999, (2): 67-69.

超低碳钢连铸结晶器用保护渣研究现状

林功文 ¹ , 吴杰 ² , 李正邦 ³ , 刘良田 ⁴ , 邱同榜 ⁵

1.钢铁研究总院

2.钢铁研究总院

3.钢铁研究总院

4.武汉钢铁(集团)公司

5.武汉钢铁(集团)公司

关键词：超低碳钢 , 结晶器保护渣 , 增碳量 , 熔渣层厚度

THE PRESENT RESEARCH OF MOLD FLUX FOR ULTRA -LOW -CARBON STEEL

分析了浇铸过程中超低碳钢液增碳的原因,介绍了国内外在防止铸坯增碳方面开展的各项工作.

参考文献

[1]	Kusano A.Improvement of Mold Fluxes for Stainless and Titanium Bearing Steels[A].,1991:147-151.
[2]	贾强.连铸结晶器中保护渣行为的理论研究[J].四川冶金,1987(01):25-33.
[3]	Terada S.Development of Mold Fluxes for Ultra-low-carbon Steels[J].Ironmaking and Steelmaking,1991(09):41-44.
[4]	Hakaru N.Characteristics of New Mold Fluxes for Strand Casting of Low and Ultra-low-carbon Steel Slabs[A].,1991:639-646.
[5]	RamaB.Optimum Selection and Application of Mold Fluxes for Carbon Steels[A].,1991:131-146.
[6]	迟景灏.连铸保护渣[M].沈阳:东北大学出版社,1993:126-129.
[7]	Lee I R.Optimization Technology of Mold Powder According to Casting Conditions[A].,1988:175-181.
[8]	Moore J A.An Overview for the Requirements of Continuous Casting Mold Fluxes[A].,1991:615-621.
[9]	陈炎.超低碳钢连铸结晶器保护渣的研究动向[J].钢铁研究,1992(05):44-47.
[10]	市川健治.发热型结晶器保护渣的开发[J].国外钢铁,1992(12):43-48.

上一张下一张

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%