本文研究了采用Sol－Gel法制备用于H2分离的Pd／γ-Al2O3复合膜的工艺过程，将含Pd2+的源物质直接加入到稳定、pH适宜的勃姆石（γ－AlOOH）溶液中，用直接浸取的方法在多孔α－Al2O3衬底上成膜．BET测试表明，复合膜的平均孔径为25～4、0nm．分析了Pd的含量和工艺参数对复合膜的形貌和结构的影响，并对膜材料进行了SEM、XRD和N2透气性能研究．
The preparation process of Pd/γ-Al2O3 composite membrane for selective hydrogen separation was studied, direct impregnation of pd was achieved by mixing the boehmite sol(γ-AlOOH) with a Pd precursor, followed by ultrasonic dispersing Pd particles uniformly throughout the membrane.The average pore diameter measured by BET was 2.5~4.0nm, SEM, XRD and separation tests were conducted in order to evaluate the properties of the composite membrane.
参考文献
| [1] | Lee S J, Yang S M, Park S B. J. Membrane Sci., 1994, 96 (3): 223--232 2 Zhao H, Xiong G, et al. Catalysis Today, 1995, 25 (3--4): 237--240 3 丁星兆, 何怡贞, 董远达. 材料科学与工程, 1994, 12 (2): 1--8 4 Chai M, Yamashita Y, Machida M, et al. J. Membrane Sci., 1994, 97: 199--207 5 夏长荣. 中国科技大学材料科学与工程系博士论文 1996年1月 6 Yoldas B E. Caram. Bull., 1975, 54: 289--293 7 周祖康, 顾惕人, 马季铭. 胶体化学基础. 北京: 北京大学出版社, 1987 8 奚同庚. 无机材料热物性学. 上海: 上海科技出版社, 1981 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%