在不同温度(300～475℃)和应变速率(0.000 5～0.1 s-1)条件下对H18热处理态的2024铝合金进行了高温拉伸试验,得到了其应力-应变曲线,结合显微组织观察分析了温度及应变速率对该铝合金流变行为的影响与高温塑性变形时的动态软化机制.结果表明:H18态2024铝合金在300℃以上高温进行塑性变形时发生了再结晶,经过475℃、应变速率0.000 5 s-1拉伸变形后,晶粒呈等轴状;其伸长率随着变形温度升高和应变速率的增大呈现先上升后下降的趋势;最大应力及应变硬化指数随温度的升高或应变速率的降低而下降;应变速率敏感指数随温度的升高而增大.
参考文献
| [1] | Serkan Toros;Fahrettin Ozturk;Ilyas Kacar .Review of warm forming of aluminum-magnesium alloys[J].Journal of Materials Processing Technology,2008(1/3):1-12. |
| [2] | 王学德,李启鹏,王路成,杨磊,胡雅骥.激光冲击强化对LY2铝合金残余应力、显微组织及疲劳性能的影响[J].机械工程材料,2012(11):82-83,96. |
| [3] | Yoshimi Tamaki .Research into achieving a lightweight vehicle body utilizing structure optimizing analysis: aim for a lightweight and high and rigid vehicle body[J].JSAE review,1999(4):558-561. |
| [4] | Li DM.;Ghosh A. .Tensile deformation behavior of aluminum alloys at warm forming temperatures[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):279-286. |
| [5] | 宋玉泉,程永春,侯磊.恒应变速率拉伸试验机的控制系统[J].中国机械工程,1999(07):782-784. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%