The solid-state graphitization process of spherical graphite iron after electropulsing pretreatment was ob- served in-situ by using a high-temperature confocal scanning laser microscope (HTCSLM). The influence of electro- pulsing pretreatment on the decomposition of cementite and the formation of graphite during the solid-state graphiti- zation was studied. The result indicates that the electropulsing pretreatment can accelerate the decomposition of ce mentite, and make more neonatal graphite in small size be formed near the cementite. The neonatal graphite nucle ates and grows chiefly at the temperature range of 800 to 850 ℃, and the average growth rate of neonatal graphite is 0. 034 μm2/s during the heating process. For the spherical graphite iron after normal and electropulsing pretreat- ment, the decomposition rate of cementite during the heating process is 0.16 and 0.24 μm2/s, respectively. Analy- sis shows that the electropulsing pretreatment promotes the dislocation accumulation near the cementite, conse- quently, the decomposition of cementite and the formation of neonatal graphite is accelerated during the solid-state graphitization.
参考文献
| [1] | Li Qingchun;Li Renxing Li;Yue Xudong et al.Effect of Electropulsing on the Formation of Graphite During Solid State Graphitization of Spherical Graphite Iron[J].Materials Chem istry and Physics,2008,112:402. |
| [2] | Li Qingchun;Li Renxing;Chang Guowei et al.Research of Microstructure of Spherical Graphite Iron by Electropulsing Annealing[J].Journal of Materials Processing Technology,2009,209:2015. |
| [3] | Li Qingchun;Chang Guowei;Zhai Qijie .Cementite Decompo-sition in Spherical Graphite Iron by Eleetropulsing[J].Journal of Materials Science and Technology,2009,25:199. |
| [4] | 吴存有,李廷举,温斌,金俊泽.强磁场对球墨铸铁退火处理的影响[J].大连理工大学学报,2004(04):514-517. |
| [5] | DOMINIC PHELAN;MARK REID;RIAN DIPPENAAR .Kinetics of the Peritectic Phase Transformation: In-Situ Measurements and Phase Field Modeling[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2006(3a):985-994. |
| [6] | G.F. Liang,C.Q. Wan,J.C. Wu,G.M. Zhu,Y. Yu,Y. Fang.IN SITU OBSERVATION OF GROWTH BEHAVIOR AND MORPHOLOGY OF DELTA-FERRITE AS FUNCTION OF SOLIDIFICATION RATE IN AN AISI304 STAINLESS STEEL[J].金属学报（英文版）,2006(06):441-448. |
| [7] | LIU Zong chang;REN Hui-ping;SONG Yi-quan.The Solid State Phase Transformation of Metal[M].北京:冶金工业出版社,2003 |
| [8] | Zhou Yizhou;Zhang Wei;Wang Baoquan;et ah .Grain Refine-ment and Formation ot" Ultrafine Grained Microstructure in a Low-Carbon Steel Under Electropulsing[J].Journal of Materi als Research,2002,17:2105. |
| [9] | Zhou Yizhou;Zhang Wei;Sui Manling et al.Formation of a Nanostructure in a Low Carbon Steel Under High Current Den-sity Electropulsing[J].Journal of Materials Research,2002,17:921. |
| [10] | Yizhou Zhou;Jingdong Guo;Wei Zhang .Influence of electropulsing on nucleation during phase transformation[J].Journal of Materials Research,2002(12):3012-3014. |
| [11] | Conrad H;Sprecher A F.Dislocations in Solids[M].Am-sterdam:The Netherlands,1989 |
| [12] | QIN Rong-shan.Investigations on the Nonequilihrium Trans-formation by Pulse Electric Current[M].Shenyang:Institute of Metal Research,Chinese Academy of Science,1996 |
| [13] | Xiao Suhong;Zhou Yizhou;Guo Jingdong et al.The Effect of High Current Pulsing on Persistent Slip Bands in Fatigued Copper Single Crystals[J].Materials Science and Engineer-ing,2002,332 A:351. |
| [14] | Languillaume J;Kapelski G;Baudelet B .Cementite Dissolu-tion in Heavily Cold Drawn Pearlitic Steel Wires[J].Acta Materialia,1997,45:1201. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%