为研究砷及铜砷共存对钢热塑性的影响,利用Gleeble-1500热模拟试验机研究了700~1100℃温度范围内含0.16% As和含0.17% Cu +0.075% As的C-Mn钢的高温塑性行为.结果表明:钢中的Cu、As引起C-Mn钢第Ⅲ脆性区向较高温度区间迁移,然而对高温抗拉强度影响不大.奥氏体+铁素体两相区薄膜状先共析铁素体沿奥氏体晶界析出导致沿晶断裂,但700℃时,由于As促进铁素体的生成,含0.16% As的C-Mn钢为韧性断裂,塑性恢复.奥氏体单相区低温域Cu、As的晶界偏聚导致含Cu、As的C-Mn钢沿晶断裂.

参考文献

[1] Matsuoka H,Osawa K,Ono M,et al .Influence of Cu and Sn on hot ductility of steels with various C content[J].ISIJ International,1997,37(3):255-262.,1997.
[2] Nagasaki C,Kihara J .Effect of copper and tin on hot ductility of ultra-low and 0.2% carbon steels[J].ISIJ International,1997,37(5):523-530.,1997.
[3] Nachtrab W T,Chou Y T .Grain boundary segregation of copper,tin and antimony in C-Mn steels at 900 ℃[J].Journal of Materials Science,1984,19(7):2136-2144.,1984.
[4] 耿明山,王新华,张炯明,王万军,肖寄光.Cu、As和Sn对低合金钢连铸坯第Ⅲ脆性区的影响[J].北京科技大学学报,2009(04):433-438.
[5] 耿明山,王新华,张炯明,王万军,肖寄光.Cu、As和Sn对低合金钢连铸坯第Ⅲ脆性区的影响[J].北京科技大学学报,2009(04):433-438.
[6] Koutnik M,Landa V(c)íHal V(c) .Koutnik M,Landa V(c)íHal V(c).The segregation of As,Sb and Bi in Cr-Ni steels and alloys with different Ni contents investigated using AES[J].Microchimica Acta,1990,101(1):121-125.,1990.
[7] Dremailova O,Emadi D,Essadiqi E,et al .Fractographic evaluation of medium carbon steels with low hot ductility[J].Microscopy and Microanalysis,2002,8:354-355.,2002.
[8] Song S H,Yuan Z X,Jia J,et al .The role of tin in the hot-ductility deterioration of a low-carbon steel[J].Metallurgical and Materials Transactions A,2003,34(8):1611-1616.,2003.
[9] Calvo J,Cabrera J M,Rezaeian A,et al .Evaluation of the hot ductility of a C-Mn steel produced from scrap recycling[J].ISIJ International,2007,47(10):1518-1526.,2007.
[10] Mintz B .The influence of composition on the hot ductility of steels and to the problem of transverse cracking[J].ISIJ International,1999,39(9):833-855.,1999.
[11] Andrews K W .Empirical Formulae for Calculation of some Transformation Temperatures[J].Journal of the Iron and Steel Institute,1965,203(7):721-727.,1965.
[12] Cowley A,Abushosha R,Mintz B .Influence of Ar3 and Ae3 temperatures on hot ductility of steels[J].Materials Science and Technology,1998,14(11):1145-1153.,1998.
[13] 冯赞,肖寄光,王福明,李长荣.砷及镧对E36船板钢连续冷却转变曲线的影响[J].金属热处理,2009(03):14-18.
[14] Ouchi C,Matusmobo K .Hot ductility in Nb bearing HSLA steels[J].Transactions of the Iron and Steel Institute of Japan,1982,22(3):181-189.,1982.
[15] Kizu T,Urabe T .Hot ductility of sulfur-containing low manganese mild steels at high strain rate[J].ISIJ International,2009,49(9):1424-1431.,2009.
[16] Vedani M,Dellasega D,Mannuccii A .Characterization of grain-boundary precipitates after hot-ductility tests of microalloyed steels[J].ISIJ International,2009,49(3):446-452.,2009.
[17] Nachtrab W T,Chou Y T .The effect of Sn,Al,and N on the hot ductility of a carbon-manganese steel between 700 ℃ and 1200 ℃[J].Metallurgical and Materials Transactions A,1988,19(5):1305-1309.,1988.
[18] Cardoso G,Mintz B,Yue S .Hot ductility of aluminium and titanium containing steels with and without cyclic temperature oscillations[J].Ironmaking & Steelmaking,1995,22(5):365-377.,1995.
[19] Mintz B,Yue S,Jonas J J .Hot ductility of steels and its relationship to the problem of transverse cracking during continuous casting[J].International Materials Reviews,1991,36(1):187-220.,1991.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%