在60℃、5MPaCO2条件下，采用高压釜试验研究了腐蚀介质的流动对X60管线钢腐蚀行为的影响。结果表明，腐蚀介质的流动导致腐蚀速率增大，但流速与腐蚀速率之间不存在线性关系；随着流速的增加，腐蚀形态呈现均匀腐蚀一局部腐蚀一均匀腐蚀的特点，腐蚀产物膜的表面和截面形貌也随之发生变化。
Using an autoclave with stirring equipment, the effect of flow velocity on the corrosion performance of X60 pipeline steel in rotating corrosion media under the condition of 60℃, 5 MPa CO2 was investigated. The results reveal that the flow of corrosion media can accelerate the corrosion rate, and the corrosion rate was nonlinear with the flow velocity. The flow of corrosion media made the corrosion mode changed from uniform corrosion to localized corrosion, and then to uniform corrosion agairn. The surface and cross-section morphology of corrosion product films also changed with the change of flow velocity.
参考文献
| [1] | 路民旭,白真权,赵新伟,赵国仙,罗金恒,陈长风.油气采集储运中的腐蚀现状及典型案例[J].腐蚀与防护,2002(03):105-113. |
| [2] | 孙丽,李长俊,彭善碧,王兵.CO2腐蚀影响因素研究[J].管道技术与设备,2008(06):35-37,48. |
| [3] | 赵学芬,姚安林,赵忠刚.二氧化碳腐蚀影响因素的层次分析法[J].腐蚀与防护,2006(04):191-193,207. |
| [4] | 周琦,贾建刚,南雪丽,赵红顺,孟倩.高温高压CO2环境介质中X60钢的腐蚀[J].腐蚀与防护,2008(12):720-723. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%