用溶液共溶沉淀法制备出纳米羟基磷灰石（n-HA）/聚酰胺46（PA46）复合材料。采用扫描电子显微镜（SEM）、燃烧试验、傅里叶变换红外光谱仪（FT-IR）、X射线衍射仪（XRD）及X射线光电子能谱仪（XPS）对复合材料的组成和界面进行了测试和表征,并对复合材料的力学性能进行了初步研究。结果表明,溶液共溶沉淀法可使n-HA颗粒均匀分散在PA46基体中,复合材料具有良好的均一性;在复合材料中n-HA与PA46界面间存在氢键,有较稳定的界面结合;复合材料有良好的力学强度,其抗拉、抗压和抗弯强度分别为67、202和146MPa,高于n-HA/聚酰胺66（PA66）复合材料。初步实验结果表明n-HA/PA46复合材料在骨组织支撑、修复和重建等承重骨部位修复方面有潜在用途。
Nano-hydroxyapatite /polyamide 46 composites were prepared in N,N-dimethylacetamide solution by co-deposition method.The composition and the interface of the two composites were analyzed by scanning electron microscope（SEM）,burning test,FT-infrared spectroscopy（FT-IR）,X-ray diffraction（XRD） and X-ray photoelectron spectroscopy（XPS）.The physical properties were characterized with tensile strength,flexural strength and compressive strength.The results showed that the n-HA particles uniformly dispersed in the composite.The SEM and XRD results indicated that the morphological and phase composition kept unchanged after combination between n-HA and PA46.The FT-IR,XRD and XPS analysis showed hydrogen bonds are found at the interface between the n-HA and PA46 in the composites.The tensile strength,compression strength and flexural strength of the n-HA/PA46 composite were about 67,202 and 146MPa.The new nano composite of n-HA/PA46 have a potential application in load bearing bone repair and replacement.
参考文献
| [1] | 许娟,汪朝阳,曹曼丽,杨喜燕,张秋琴,黎燕凌.羟基磷灰石/聚乳酸类复合材料[J].化工科技,2003(03):44-47. |
| [2] | 严永刚,李玉宝,汪建新,冯建清,黄玫,K.de Groot.聚酰胺-66/羟基磷灰石复合材料的制备和性能研究[J].塑料工业,2000(03):38-40. |
| [3] | 蒋电明,权正学,欧云生,倪卫东,梁熙.n-HA/PA66复合生物活性支撑材料在重建椎体结构中的初步临床应用[J].重庆医学,2007(11):1010-1012. |
| [4] | 王群波,蒋电明,安洪,李智,何秦,张东,向世群,吴晓兰,朱小玲.纳米羟基磷灰石/聚酰胺66复合人工椎体在胸腰椎骨折中的应用[J].中华创伤杂志,2005(09):690-692. |
| [5] | 马建民,宋诗文,郭健.新型耐热尼龙[J].现代塑料加工应用,2003(02):41-44. |
| [6] | 袁绍彦,刘奇祥,叶南飙,黄锐.耐高温聚酰胺的性能及应用[J].中国塑料,2009(10):6-9. |
| [7] | 张翔,李玉宝,吕国玉,左奕,牟元华,吴兰.n-HA/PA66复合材料中两相间作用机理研究[J].功能材料,2005(06):896-899. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%