Cell attachment and spreading on Ti-based alloy surfaces is a major parameter in implant technology. Ti39Nb-13Ta-4.6Zr alloy is a new β type Ti alloy developed for biomedical application. This alloy has low modulus and high strength, which indicates that it can be used for medical purposes such as surgical implants.To evaluate the biocompatibility and effects of the surface morphology of Ti-39Nb-13Ta-4.6Zr on the cellular behaviour, the adhesion and proliferation of rat gingival fibroblasts were studied with substrates having different surface roughness and the results were also compared with commercial pure titanium and Ti-6Al-4V. The results indicate that fibroblast shows similar adhesion and proliferation on the smooth surfaces of commercial pure titanium (Cp Ti), Ti-39Nb-13Ta-4.6Zr, and Ti-6Al-4V, suggesting that Ti-39Nb-13Ta-4.6Zr has similar biocompatibility to Cp Ti and Ti-6Al-4V. The fibroblast adhesion and spreading was lower on rough surfaces of Cp Ti, Ti-39Nb-13Ta-4.6Zr and Ti-6Al-4V than on smooth ones. Surface roughness appeared to be a dominant factor that determines the fibroblast adhesion and proliferation.
参考文献
| [1] | J B Brunski;D A Puleo .[J].International Journal of Oral and Maxillofacial Implants,2000,15:15. |
| [2] | D A Puleo;A Nanci .[J].Biomaterials,1999,20:2311. |
| [3] | Z Schwartz;B D Boyan .[J].Journal of Cellular Biochemistry,1994,56:340. |
| [4] | B Groessner-Schreiber;R S Tuan .[J].Journal of Cell Science,1992,101:209. |
| [5] | J Y Martin;Z Schwartz;T W Hummert;D M Schraub, J Simpson, Jr J Lankford,D D Dean,D L Cochran, B D Boyan .[J].Journal of Biomedical Materials Research,1995,29:389. |
| [6] | D D Deligianni;N Katsala;S Ladas;D Sotiropoulou, J Amedee, Y F Missirlis .[J].Biomaterials,2001,22:1241. |
| [7] | K Matsuzaka;X F Walboomers;M Yoshinari;T Inoue, J A Jansen .[J].BIOMATERIALS,2003,24:2711. |
| [8] | J E Davies .[J].International Journal of Prosthodontics,1998,11:391. |
| [9] | S J Li;Y L Hao;R Yang;Y Y Cui, M Niinomi .[J].Materials Transactions,2002,43(12):2964. |
| [10] | S. J. Li;R. Yang;M. Niinomi .Phase transformation during aging and resulting mechanical properties of two Ti-Nb-Ta-Zr alloys[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2005(6):678-686. |
| [11] | G Welsch;R Boyer;E W Collings.Material Properties Handbook[M].Titanium Alloys,ASM,Metals Park,Oh,1994 |
| [12] | S. J. Li;R. Yang;S. Li;Y. L. Hao;Y. Y. Cui;M. Niinomi;Z. X. Guo .Wear characteristics of Ti-Nb-Ta-Zr and Ti-6Al-4V alloys for biomedical applications[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2004(9/10):869-876. |
| [13] | M Long;H J Rack .[J].Biomaterials,1998,19:1621. |
| [14] | S A Shabalovskaya .[J].Biomedical Materials & Engineering,1996,6:267. |
| [15] | D M Brunette;P Tengvall;M Textor;P Thomsen.Titanium in Medicine Material Science,Surface Science,Engineering,Biological Responses and Medical Applications[M].Springer-Verlag Berlin Heidelberg,2001 |
| [16] | D M Brunette .[J].Experimental Cell Research,1986,167:203. |
| [17] | M Hormia;M Kononen;J Kivilahti;I Virtanen .[J].Journal of Periodontal Research,1991,26:491. |
| [18] | K Anselme;M Bigerelle;B Noel;E Dufresne, D Judas, A Iost, P Hardouin .[J].Journal of Biomedical Materials Research,2000,49:155. |
| [19] | K Kieswetter;Z Schwartz;T W Hummert;D L Cochran, J Simpson, D D Dean, B D Boyan .[J].Journal of Biomedical Materials Research,1996,32:55. |
| [20] | J Y Martin;Z Schwartz;T W Hummert;D M Schraub, J Simpson, J Lankford, D D Dean, D L Cochran, B D Boyan .[J].Journal of Biomedical Materials Research,1995,29:389. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%