采用XRD、SEM、DSC等测试分析手段研究了Ca/Si比变化对CBS微晶玻璃晶相、微观结构和电性能的影响。结果表明在固定B2O3的含量为17%(摩尔分数)时,发现当m(Ca/Si比)〈1.08时,CBS微晶玻璃的烧结温度〉900℃,当m〉1.08时,CBS微晶玻璃的烧结温度900℃。当m达到1.767时,CBS微晶玻璃无法烧结;随着CaO含量的增加,Ca2SiO4晶体逐渐增加,硅灰石相逐渐减少,石英相逐渐增加;在1MHz下,C2、C5和C7试样烧结后电损耗均〈2×10-3。

Influence of Ca/Si on the crystallization,microstructure and dielectric properties of CaO-B2O3-SiO2 glass was studied by using XRD,DSC and SEM.The results indicate that when m(Ca/Si ratio)1.08,calcium borosilicate glass sintering temperature higher than 900℃,but it is m1.08,CBS department of the sintering temperature of glass is far lower at 900℃.When m reaches 1.767,CBS can not be sintered;with the increase of CaO content,Ca2SiO4 crystals gradually increased,leading to the gradual reduction of wollastonite phase,resulting in gradual increase in quartz;the samples were C2,C5,C7 dielectric loss sintered 2×10-3 at 1MHz.

参考文献

[1] 朱海奎,刘敏,周洪庆.LTCC介质材料的研究进展[J].材料导报,2006(z1):328-330.
[2] 吕安国,王美娜,丘泰,周洪庆,刘敏.烧结助剂对硼硅钙微晶玻璃结构和介电性能的影响[J].硅酸盐学报,2007(01):60-64.
[3] 许贵军,周洪庆,朱海奎,陈栋,刘敏.CaO-B2O3-SiO2系玻璃形成区及性能研究[J].电子元件与材料,2009(05):47-49.
[4] 胡一晨,孙丽娟,张计发,张耒.低温共烧CaO-B2O3-SiO2系统微晶玻璃的分相与析晶[J].玻璃与搪瓷,2009(03):14-19.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%