Aligned Solidification Structure of the MnBi Phase in Semisolidified Bi-Mn Alloy with a Static Magnetic Field

材料科学技术（英文）, 2004, 20(3): 311-314.

^1, , ^2, , ^3, , ^4,

1.Department of Materials Science and Engineering, Shanghai University, Shanghai,200072, China

2.Department of Materials Science and Engineering, Shanghai University, Shanghai,200072, China

3.Department of Materials Science and Engineering, Shanghai University, Shanghai,200072, China

4.Department of Materials Science and Engineering, Shanghai University, Shanghai,200072, China

基金项目: "Shu Guang" Shanghai Education Development Foundation(98SG37) 国家自然科学基金(59871026,50225416,50234020)

Aligned Solidification Structure of the MnBi Phase in Semisolidified Bi-Mn Alloy with a Static Magnetic Field

Keywords： Magnetic field

The solidification structure of Bi-3 wt pct Mn alloy grown up in the semisolid zone under the influence of a static magnetic field (up to 1.0 T) and the relation of the magnetic property with the solidification structure have been investigated experimentally. It was shown that the primary phase MnBi crystals in the alloy aligned and oriented along the direction of the applied magnetic field. The orientating tendency and the average length of the elongated MnBi crystals increased with the increase of the applied field and the solidification time. Moreover, the remanence of the alloy along the aligned direction of the MnBi phase in the case of solidification with a magnetic field was apparently anisotropic and nearly double of that without the magnetic field. This indicated that the MnBi crystals oriented and aligned along their easy magnetization axis. A model was proposed to explain the alignment and orientation growth of the MnBi crystals in a magnetic field in terms of the magnetic anisotropy of the crystals and the magnetic interaction between them.

参考文献

[1]	P Gillon .[J].Journal of The Minerals,Metals & Materials Society,1995,47:34.
[2]	A.E.Mikelson;Y.K.Karklin .[J].Journal of Crystal Growth,1981,52:524.
[3]	P D Rango;M.Lee;P.Lejay;A.Sulpice,R.Tournier,M.Ingold,P.Germi M.Pernet .[J].Nature,1991,349:770.
[4]	A.Katsuki;R.Tokunaga;S.I.Watanabe.[J].Chemistry Letters,1996(08):607.
[5]	M N Shetty;DKRawat;K N Rai .[J].Journal of Materials Science,1987,22:1908.
[6]	H Morikawa;K.Sassa;S.Asai .Mater Trans[J].Materials Transactions-Japan Institute of Metals,1998,39:814.
[7]	H Yasuda;I.Ohnaka;K.Shimamura.in Proc 3rd Int Conf on EPM[J].Nagoyaed S Asai,2000:647.
[8]	HuiWANG;Zhongming REN;Guochang JIANG .Mater Sci Eng[J].Materials Science and Engineering,2001,19(119)
[9]	HuiWANG;Zhongming REN;Guochang JIANG 等.[J].Chinese Science Abstract,2000,6:240.
[10]	X Guo;ZAltounian;J O S Olsen .[J].Journal of Applied Physics,1991,69:6067.
[11]	W G Moffatt.The Handbook of Binary Phase Diagrams[J].USAGenium,1984:11/83.
[12]	DefuWAN;Shihua LUO.[M].北京:Physics of Magnetism Electronic Industry Press,1987

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Aligned Solidification Structure of the MnBi Phase in Semisolidified Bi-Mn Alloy with a Static Magnetic Field

参考文献