对经过固溶处理的2906超级双相不锈钢材料进行750℃下不同时间(2、6和10 h)的时效处理,利用OM、XRD、SEM、EDS和电化学工作站分析了时效时间对金属间相、力学性能和耐蚀性能的影响.结果表明:在750℃时效处理时,组织中生成σ相和γ2相,σ相和γ2相含量随着时效时间的延长而增多;时效时间越长,试样的抗拉强度及耐蚀性越差,硬度越高.
参考文献
| [1] | 吴玖.双相不锈钢[M].北京:冶金工业出版社,1999 |
| [2] | M. Campos;A. Bautista;D. Caceres .Study of the interfaces between austenite and ferrite grains in P/M duplex stainless steels[J].Journal of the European Ceramic Society,2003(15):2813-2819. |
| [3] | Hua Tan;Yiming Jiang;Bo Deng .Effect of annealing temperature on the pitting corrosion resistance of super duplex stainless steel UNS S32750[J].Materials Characterization,2009(9):1049-1054. |
| [4] | 向红亮,黄伟林,刘东,何福善.N含量对29Cr铸造超级双相不锈钢组织及性能的影响[J].金属学报,2010(03):304-310. |
| [5] | Xiang H L;Liu D;Huang W L et al.Effects of N content on microstructure and properties of SAF2906 casting super duplex stainless steel after cryogenic treatment[J].Advanced Materials Research,2010,139-141:670-676. |
| [6] | Holmberg B;Sun C C.[A].Beijing:Stainless Steel Council China Special Steel Enterprises Association,2006 |
| [7] | 马玉喜,荣凡,周荣,蒋业华.固溶时效对超高氮奥氏体不锈钢析出行为的影响[J].材料热处理学报,2008(03):66-70. |
| [8] | 向红亮,何福善,刘东.时效温度对铸造超级双相不锈钢析出相的影响[J].金属学报,2009(12):1456-1460. |
| [9] | Badji R;Bouabdallah M;Bacroix B .Effect of solution treatment temperature on the precipitaiton kinetic of σ-phase in 2205 duplex stainless steel welds[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2008,06(24) |
| [10] | 索科尔ия.双相不锈钢[M].北京:原子能出版社,1979 |
| [11] | 陆卫东,乐平,刘雪燕,郁凉峰,邬彤.00Cr22Ni5Mo3N双相不锈钢的组织分析[J].热处理,2008(01):37-46. |
| [12] | 向红亮,黄伟林,刘东,何福善.铸造SAF2906不锈钢在人工海水中的电化学阻抗谱[J].材料热处理学报,2013(01):81-85. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%