The impact properties of hot rolled carbon steel （used for the manufacture of reinforcement steel bars） and the quenched ＆ tempered （Q＆T） low alloy steel （used in the pressure vessel industry） were determined. The microstructure of the hot rolled carbon steel contained ferrite/pearlite phases, while that of the quenched and tempered low alloy steel contained bainite structure. Impact properties were determined for both steels by instrumented impact testing at temperatures between -150 and 200℃. The impact properties comprised total impact energy, ductile to brittle transition temperature, crack initiation and propagation energy, brittleness transition temperature and cleavage fracture stress. The Q＆T low alloy steel displayed much higher resistance to ductile fracture at high test temperatures, while its resistance to brittle fracture at low test temperatures was a little higher than that of the hot rolled carbon steel. The results were discussed in relation to the difference in the chemical composition and microstructure for the two steels.
参考文献
| [1] | H. K. D. H. Bhadeshia .The bainite transformation: unresolved issues[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(0):58-66. |
| [2] | B K PANIGRAHI .Processing of low carbon steel plate and hot strip/an overview[J].Bulletin of Materials Science,2001(4):361-371. |
| [3] | S.J. Wu;J.F. Knott .On the statistical analysis of local fracture stresses in notched bars[J].Journal of the Mechanics and Physics of Solids,2004(4):907-924. |
| [4] | M.N. SHABROV;E. SYLVEN;S. KIM .Void Nucleation by Inclusion Cracking[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2004(6):1745-1755. |
| [5] | M. Rakin;Z. Cvijovic;V. Grabulov .The Influence of Microstructure on Ductile Fracture Initiation in Low-Alloyed Steel[J].Materials Science Forum,2004(0):175-180. |
| [6] | M. Jahazi;B. Eghbali .The influence of hot forging conditions on the microstructure and mechanical properties of two microalloyed steels[J].Journal of Materials Processing Technology,2001(1/3):594-598. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%