利用冷压-烧结技术制备了CuO 掺杂的10NiO-NiFe2O4复合陶瓷,研究了CuO 掺杂量对10NiO-NiFe2O4复合陶瓷物相组成、显微结构、致密度及导电率的影响.结果表明:当CuO掺杂量为0～12.5%(质量分数)时, 烧结样品中主要含有NiO、Cu和NiFe2O4、CuO在氮气气氛下分解为金属Cu,在烧结温度下为液相促进了致密化烧结;1473K烧结时,8.75%CuO掺杂样品的相对密度最大,达到94.43%,比未掺杂样品的相对密度提高了18.16%;当CuO掺杂量为4%时,在1233K温度下样品达到最大导电率5.169S/cm,是未掺杂样品的导电率1.026S/cm的5倍.
参考文献
| [1] | Pawlek R P.Inert anodes:an Update[A].USA:TMS,2002:449-456. |
| [2] | Weyand J D;DeYoung D H;Ray A P et al.Inert Anodes for Aluminium Smelting[R].Washington D C:Aluminum Company of America,1986. |
| [3] | Pawlek R P;Hale W R.Inert Anodes for the Primary Aluminum Industry:an update[A].USA:TMS,1996:243-248. |
| [4] | LI Jie;LAI Yan-qing;ZHOU Ke-chao;LI Zhi-you;LIU Ye-xiang .Preparation and preliminary testing of cermet inert anode for aluminum electrolysis[J].Transactions of Nonferrous Metals Society of China,2003(3):663-670. |
| [5] | Keniry J .[J].JOM-Journal of the Minerals Metals and Materials Society,2001,53(05):43-47. |
| [6] | Sadoway D R .[J].JOM-Journal of the Minerals Metals and Materials Society,2001,53(05):34-35. |
| [7] | 席锦会,姚广春,刘宜汉,张晓明.五氧化二钒对铁酸镍基金属陶瓷惰性阳极导电行为的影响[J].硅酸盐学报,2006(01):34-38. |
| [8] | 田忠良,赖延清,段华南,孙小刚,张刚.掺杂SnO2对NiFe2O4陶瓷电导率的影响[J].矿产保护与利用,2004(05):37-40. |
| [9] | 张剑红,刘宜汉,席锦会,姚广春.掺杂TiO2的镍铁尖晶石的高温导电性[J].材料与冶金学报,2003(04):271-273. |
| [10] | 赖延清,张勇,张刚,李劼,贺跃辉,黄伯云,刘业翔.CaO掺杂对10NiO-NiFe2O4复合陶瓷烧结致密化的影响[J].中国有色金属学报,2006(08):1355-1360. |
| [11] | 赖延清,张刚,李劼,刘业翔.金属含量对Cu-Ni-NiFe2O4金属陶瓷导电性能的影响[J].中南大学学报（自然科学版）,2004(06):880-884. |
| [12] | 张雷,周科朝,李志友,张晓泳.气氛对NiFe2O4陶瓷烧结致密化的影响[J].中国有色金属学报,2004(06):1002-1006. |
| [13] | 李英;龚江宏;唐子龙 等.[J].硅酸盐学报,1997,25(06):705-710. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%