Stress Corrosion of X80 Pipeline Steel Welded Joints by Slow Strain Test in NACE H2S Solutions

钢铁研究学报(英文版), 2013, 20(1): 40-46.

^1, , ^2, , ^3,

1.College of Mechanical Engineering, Changzhou University, Changzhou 213016, Jiangsu, China

2.College of Mechanical Engineering, Changzhou University, Changzhou 213016, Jiangsu, China

3.College of Mechanical Engineering, Changzhou University, Changzhou 213016, Jiangsu, China

基金项目: Innovation Program of Graduated Student of Jiangsu Province of China(CXZZ12-731,CXLX11-0388) Item Sponsored by Natural Science Foundation of Jiangsu Province of China(BK2009104)

Stress Corrosion of X80 Pipeline Steel Welded Joints by Slow Strain Test in NACE H2S Solutions

KONG De-jun ^1, , WU Yong-zhong ^2, , LONG Dan ^3,

1.College of Mechanical Engineering, Changzhou University, Changzhou 213016, Jiangsu, China

2.College of Mechanical Engineering, Changzhou University, Changzhou 213016, Jiangsu, China

3.College of Mechanical Engineering, Changzhou University, Changzhou 213016, Jiangsu, China

Keywords： submerged arc welding

参考文献

[1]	Ping Liang,Cui-wei Du,Xiao-gang Li,Xu Chen,Zhang liang.Effect of hydrogen on the stress corrosion cracking behavior of X80 pipeline steel in Ku'erle soil simulated solution[J].矿物冶金与材料学报,2009(04):407-413.
[2]	Moro, I.;Briottet, L.;Lemoine, P.;Andrieu, E.;Blanc, C.;Odemer, G. .Hydrogen embrittlement susceptibility of a high strength steel X80[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(27/28):7252-7260.
[3]	X.B. Yang;Z. Zhuang;X.C. You .Dynamic fracture study by an experiment/simulation method for rich gas transmission X80 steel pipelines[J].Engineering Fracture Mechanics,2008(18):5018-5028.
[4]	陈翠欣,李午申,王庆鹏,冯斌,刘方明,薛振奎.X80管线钢焊接粗晶区韧化因素的研究[J].材料工程,2005(05):22-26.
[5]	Yongxing Wang;Weimin Zhao;Hua Ai;Xiaoguang Zhou;Timing Zhang .Effects of strain on the corrosion behaviour of X80 steel[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2011(9):2761-2766.
[6]	Ping Liang;Xiaogang Li;Cuiwei Du;Xu Chen .Stress Corrosion Cracking Of X80 Pipeline Steel In Simulated Alkaline Soil Solution[J].Materials & design,2009(5):1712-1717.
[7]	H.B. Xue;Y.F.Cheng .Characterization of inclusions of X80 pipeline steel and its correlation with hydrogen-induced cracking[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2011(4):1201-1208.
[8]	李云涛,杜则裕,陶勇寅,熊林玉.X70管线钢硫化氢应力腐蚀[J].焊接学报,2003(03):76-78,86.
[9]	周贤良,李晖榕,华小珍,叶志国.X80管线钢埋弧焊焊接接头的组织和腐蚀性能[J].焊接学报,2011(01):37-40,80.
[10]	Revie R W .Hydrogen-Induced Cracking of Linepipe Steels Used in Sour Service[J].Corrosion,1993,49(07):531.
[11]	DONG Jun-ming;PAN Xi-de;FAN Pei-li et al.Stress Corrosion Cracking of Low Alloy Steels and Welded Joints in Sea Water[J].Journal of Xi'an Jiaotong University,1998,32(07):99.
[12]	毕凤琴,张旭昀,王勇,孙丽丽,汪洋.X70管线钢在湿H2S环境中的应力腐蚀行为研究[J].材料工程,2009(08):15-18,23.
[13]	黄春波,李光福,杨武.X70管线钢焊缝应力腐蚀破裂的研究[J].腐蚀与防护,2005(01):1-5.
[14]	张骁勇,高惠临,毕宗岳,徐学利,张莉莉.焊接热输入对X80焊管焊缝组织与性能的影响[J].材料工程,2010(09):66-70.
[15]	王亚男,王春怀,唐继权,刘春明.X65管线钢抗H2S腐蚀的试验研究[J].东北大学学报(自然科学版),2004(05):420-423.
[16]	周建江,刘杏,李光福,郭浩,杨武.X70管线钢在近中性及高pH值溶液中的电化学行为和SCC敏感性[J].腐蚀与防护,2007(01):1-5.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Stress Corrosion of X80 Pipeline Steel Welded Joints by Slow Strain Test in NACE H2S Solutions

参考文献