The mechanical properties of calcium (Ca) microalloyed 24 carat gold (Au99.9Ca0.1) were measured and the corresponding microstructure was observed by TEM in order to investigate the strengthening mechanism.It was observed that the microalloying of 0.1wt％ Ca improved the tensile strength (by 79％ and 57％ for the rolling and annealing states,respectively),hardness and E-Modulus as well as reduced the ductility of the 24 carat Au.Dispersed nano-sized precipitates and high density deformation twins were found in the rolled Au99.9Ca0.1,which are attributed to be the major strengthening factors.The twins subsided after annealing and the strengthening of the annealed Au99.9Ca0.1 is mainly contributed by the coarsened semi-coherent precipitates.
参考文献
| [1] | Corti C W .Metallurgy of Microalloyed 24 Carat Golds[J].Gold Bulletin,1999,32(02):39-47. |
| [2] | Zhao H;Ning Y.Gold[M].长沙:中南大学出版社,2003 |
| [3] | Corti C W .Strong 24 carat golds:The metallurgy of microalloying[J].Gold Technology,2001,33:27. |
| [4] | Herklotz G;Schrapler L;Simons C et al.[P].U.S.Paten,.No.6,242,106 B1,2001. |
| [5] | Tomohiro U;Kohei T .[P].U.S.Patent,No.6,080,492,2000. |
| [6] | Chew Y H;Wong C C;Breach C D et al.Effect of Ca on grain boundary cohesion in Au ballbonding wire[J].Thin Solid Films,2006,504:346-349. |
| [7] | Y. H. Chew;C.C. Wong;C.D. Breach .Effects of calcium on the mechanical properties of ultra-fine grained gold wires[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2006(1/2):193-197. |
| [8] | L. Lu;X. Chen;X. Huang;K. Lu .Revealing The Maximum Strength In Nanotwinned Copper[J].Science,2009(5914):607-610. |
| [9] | Shuichi Mitoma;Ichimitsu Itabashi;Shin Takaura .Effects of Trace Added Calcium or Palladium on Annealing Characteristics of Cold - Worked Pure Gold[J].日本金属学会誌,2002(7):754-759. |
| [10] | Fleischer R L;D.Peckner.Strengthening of Metals[M].New York:Reinhold,1964:114-117. |
| [11] | Okamoto H;Massalski T B.Phase diagrams of binary gold alloys[M].ASM International,Ohio:Metals Park,1987 |
| [12] | N. Stanford;M.R. Barnett .Effect of particles on the formation of deformation twins in a magnesium-based alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2009(1/2):226-234. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%