通过两道次压缩变形实验对含Nb微合金钢静态软化行为进行了研究.结果表明:含Nb微合金钢静态再结晶临界温度随应变量增大而降低;随原始奥氏体晶粒尺寸增加而升高.温度高于静态再结晶临界温度时,含Nb微合金钢的静态再结晶激活能为常数(170.589 kJ/mol);温度低于静态再结晶临界温度时,由于Nb的碳氮化物应变诱导析出,含Nb微合金钢的静态再结晶激活能为温度的函数,静态再结晶临界温度可通过再结晶激活能与温度倒数的关系曲线来确定.
参考文献
| [1] | G.LI;T.M.Maccagno .Effect of Initial Grain Size on the Static Recrystallization Kinetics of Nb Microalloyed Steels[J].ISIJ International,1996(12):1479-1485. |
| [2] | 周晓光,刘振宇,吴迪,王国栋.薄板坯连铸连轧过程中的静态软化行为[J].东北大学学报(自然科学版),2007(10):1374-1377. |
| [3] | 孙彬斌,贾志伟,张红梅,刘振宇,王国栋.C-Si-Mn系双相钢静态软化行为的研究[J].热加工工艺,2007(10):21-24. |
| [4] | Medina S F;Mancilla J E .Determination of Static Recrystallization Critical Temperature of Austenite in Microalloyed Steels[J].ISIJ International,1993,33(12):1257. |
| [5] | S. F. MEDINA;J. E. MANCILLA .Static Recrystallization Modelling of Hot Deformed Microalloyed Steels at Temperatures below the Critical Temperature[J].ISIJ International,1996(8):1077-1083. |
| [6] | L.Q. Ma,Z.Y. Liu,S.H. Jiao,X.Q. Yuan,D. Wu.MODELING OF STATIC RECRYSTALLIZATION KINETICS OF Nb-BEARING STEELS[J].金属学报（英文版）,2006(04):271-278. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%