Study on High Toughness HSLA-80 Steel

对一种HSLA-80钢板分别进行了调质处理和直接淬火加回火工艺的比较性试验研究.常规调质处理钢板在满足强度要求的同时可以获得夏比冲击功AKV(-85℃)=300 J以上的高韧性,同时具有100%的纤维状断口.而直接淬火加回火工艺可以获得更高的屈服强度,同时仍具有在-85℃可以接受的冲击韧性.