利用鞣制化学中铝鞣机理,将Al（Ⅲ）络合在明胶水解得到的胶原蛋白分子上,制备Al（Ⅲ）改性胶原蛋白絮凝材料,利用XRD、荧光光谱和XPS对产物结构及作用机理进行表征与分析。将所制备的絮凝剂用于油田废弃钻井液的絮凝,以其CODCr去除率和悬浮物含量为指标,考察了絮凝条件对废弃钻井液处理效果的影响。结果表明胶原蛋白分子与Al（Ⅲ）间发生了配位反应,制备出了Al（Ⅲ）改性胶原蛋白絮凝剂。其用于废弃钻井液絮凝时,用量为20.7g/L,pH值为6～9,温度为20～40℃。絮凝后,废弃钻井液CODCr去除率达80.1%,悬浮物含量从初始的2115mg/L降至190mg/L,絮凝效果明显。
Under aluminium tanning mechanism in tanning chemical,Al（Ⅲ） was combined on collagen protein which obtained by the hydrolysis of gelatin.So Al（Ⅲ） modified collagen flocculant was prepared.The structure of products and the reaction mechanism are characterized and analyzed by XRD,fluorescence spectrum and XPS.When using the prepared flocculant in the treatment of waste drilling water,the influence of flocculation conditions on the treatment effect was studied by CODCr removal rate and suspended solids content.The result indicated that a coordination reaction occurred between collagen protein and Al（Ⅲ）.When used to flocculate waste drilling water,the dosage of the prepared flocculant was 20.7g/L,pH was 6-9 and temperature was 20-40℃.After flocculation,the CODCr removal rate was 80.1% and suspended solids content decreased from 2115mg/L to 190mg/L.
参考文献
| [1] | Jones F V;Rushing J H;Churan M A.The chronic toxicity of mineral oil-wet and synthetic liquid-wet cuttings on an estuarine fish[A].Hague,1991 |
| [2] | 成都金池塘科技有限公司 .钻井废弃泥浆无害化处理技术方案[R].成都:成都金池塘科技有限公司,2009. |
| [3] | Andrew K;Woitanowicz.Oilfield enviormental controltechnology[J].Journal of Petroleum Technology,1993(02):166-173. |
| [4] | 赵雄虎,王风春.废弃钻井液处理研究进展[J].钻井液与完井液,2004(02):43-48. |
| [5] | Mallon;Joseph J .Cationic water-soluble polymer precipitation in salt solution[P].USP:6013708,2000-01-11. |
| [6] | 方振华,刘志勇,吴学玲.淀粉基阳离子絮凝剂的研制及性能测试[J].化学研究与应用,2009(06):930-933. |
| [7] | 廖乾邑,朱明,冯西宁,魏玉君,张春晓,宁海峰.两性高分子絮凝剂的研究现状[J].应用化工,2008(01):90-92. |
| [8] | 蒋挺大.胶原与胶原蛋白[M].北京:化学工业出版社,2006:56. |
| [9] | Taylor L M M;Cabeza F .Preparation of high molecular weight products by crosslinking protein isolated from the enzymatic processing of chromium-containing collagenousmaste:modification of gelatin[J].Leather Science and Engineering,2005,6(15):3-8. |
| [10] | 陈武勇;李国英.鞣制化学[M].北京:中国轻工业出版社,2005 |
| [11] | Teng S H;Lee E J;Wang P .Collagen/hyroxyapatite composite nanofibers by electrospinning[J].Materials Letters,2008,62(17-18):3055-3058. |
| [12] | Y. Tanaka;Tanaka;M;Nakai;T;Akahori;M;Niinomi;Y;Tsutsumi;H;Doi;T;Hanawa;M. Nakai;T. Akahori;M. Niinomi;Y. Tsutsumi;H. Doi;T. Hanawa .Characterization Of Air-formed Surface Oxide Film On Ti-29nb-13ta-4.6zr Alloy Surface Using Xps And Aes[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(8):2111-2116. |
| [13] | Gurdak E;Rouxhet PG;Dupont-Gillain CC .Factors and mechanisms determining the formation of fibrillar collagen structures in adsorbed phases[J].Colloids and Surfaces, B. Biointerfaces,2006(1):76-88. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%