研究了不同输入电流下激光刻痕对取向硅钢表面绝缘涂层的影响,分析了刻痕宽度、刻痕深度和磁性能随电流的变化规律及刻痕对绝缘涂层的破坏程度,并对刻痕后的取向硅钢样品进行退火,研究刻痕后磁畴粗化规律,对激光刻痕的耐热性进行分析.结果表明:随着电流的增大,刻痕的宽度和深度增大,刻痕对绝缘涂层的损伤严重.激光刻痕样品在500℃以上的温度下进行去应力退火,磁畴开始粗化,铁损较刻痕后升高.确定了磁畴粗化定量关系.随着退火温度升高,磁畴宽度增大,铁损升高的幅度增大.
参考文献
| [1] | 何忠治,赵宇,罗海文.电工钢[M].北京:冶金工业出版社,2012.,2012. |
| [2] | 朱业超,王良芳,乔学亮.表面处理细化取向硅钢磁畴的方法与机理[J].钢铁研究,2006(06):50-53. |
| [3] | Luchi T,Yamaguchi S,Ichiyama T,et al .Laser processing for reducing core loss of grain oriented silicon steel[J].Journal of Applied Physics,1982,53(3):2410-2412.,1982. |
| [4] | Ponnaluri S V,Cherukuri R,Molian P A .Core loss reduction in grain-oriented silicon steels by excimer laser scribing Part I experimental work[J].Journal of Materials Processing Technology,2001,112:199-204.,2001. |
| [5] | Huang Y,Ming W,Li M,et al .Parameter optimization of Nd:Yag laser scribing process on core loss of grain-oriented magnetic silicon steels[J].The International Journal of Advanced Manufacturing Technology,2014,70:1-9.,2014. |
| [6] | 刘新彬,孔祥华,何业东,张鲲,王向欣,胡守天,杨浩.氮化硅张力涂层对取向硅钢性能的影响[J].材料热处理学报,2007(06):128-130. |
| [7] | 胡守天,孔祥华,李平和,赵启博,杨皓,王向欣,何业东.取向硅钢绝缘涂层结构及其对铁芯损耗的影响[J].北京科技大学学报,2009(10):1277-1280. |
| [8] | Ahn S,Kim D W,Kim H S,et al .Investigation of core loss characteristics of 3% SiFe using the laser scribing method[J].Physica status solidi(b),2004,241(7):1641-1644.,2004. |
| [9] | Neisheisel G L,Schonen J W.Laser treatment of electrical steel:US,Patent,4456812[P].1984-6-26.,1984. |
| [10] | 祁烁,王丽芝.关于激光刻痕处理取向硅钢的时效性质的研究[J].沈阳化工学院学报,2002(02):147-149. |
| [11] | 杨玉玲,孙凤久,张瑞峰,齐小龙.激光局部氮化改善取向硅钢磁畴结构分布[J].东北大学学报(自然科学版),2002(02):189-191. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%