酸洗是钛带冷轧前的重要工序之一，首先从酸的浓度及配比、酸洗时间、酸洗温度等方面对热轧退火后钛带卷的酸洗条件进行了实验室探究。结果表明，随着氢氟酸与硝酸体积比的降低，钛带的酸洗失重率逐渐降低，而酸洗所需时间逐渐增加。综合考虑酸洗的效果、速度及成本认为最佳酸洗工艺条件是：酸洗温度为40℃，酸洗液中氢氟酸体积分数为3％、硝酸体积分数为27％，酸洗时间为240 s时，酸洗效果最佳，此时，钛带试样失重率为1.12％。此外，研究发现，酸洗温度为25℃和55℃皆不利于钛带酸洗。之后，工业化试验表明，按照最佳的酸洗工艺条件对工业纯钛带进行酸洗，酸洗效果较好，表面氧化皮可被彻底洗尽。
Pickling is one of the important processes before titanium strip coil cold rolling .Pickling conditions for hot rolled annealed titanium strip coil were first studied in laboratory , including the concentration of acid , pickling time , pickling temperature and so on .The results show that the rate of weight loss will decrease while the pickling time will increase with the decreasing of the ratio of HF∶HNO3 .The best condition for pickling is that the concentration of HF acid is 3%and HNO3 acid is 27%, the pickling temperature is 40 ℃and the pickling time is 240 s.And under this treat condition, the rate of weight loss will only be 1.12%.Besides, the pickling temperature of 25 ℃and 55 ℃are both not benefit for the pickling of titanium strip coil .The industrialized experiment results show that the pickling effect is obvious based on the best treat condition , and the surface oxide layer can be removed thoroughly .
参考文献
| [1] | 杜礼章.工业纯钛板材生产工艺研究[J].特钢技术,2008(04):19-21. |
| [2] | 薛小莲.工业纯钛带材的加工工艺[J].冶院科技,1994(04):43-46. |
| [3] | 徐信.纯钛卷酸洗工艺浅析[J].化学与工程装备,2011(07):163-164. |
| [4] | Johnson J W;Shen K S;James W J .A kinetic study of the oxidation of Ti(III) to Ti(IV) in hydrofluoric acid solutions[J].Journal of the Less-Common Metals,1968,15(02):177-182. |
| [5] | Sutter E M M;Goetz-Grandmont G J .The behaviour of tita-nium in nitric-hydrofluoric acid solutions[J].Corrosion Sci-ence,1990,30(4/5):461-476. |
| [6] | 朱立;孙本良.钢铁酸洗技术[M].北京:化学工业出版社,2007:22. |
| [7] | 黄德明.工业纯钛TA2的氧化行为研究[J].钢铁钒钛,2010(01):11-16. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%