以Ti和B4C为起始反应物,分别在常规和超重力条件下通过燃烧合成技术制备出Ti(C,N)-TiB2复合粉体,利用XRD和SEM对燃烧产物进行了表征,研究了起始组成和超重力条件对燃烧产物相组成和微观形貌的影响.结果表明,燃烧产物主要由Ti(C,N)和TiB2组成,通过改变起始配方中Ti/B4C的摩尔比,可以调节产物中Ti(C,N)和TiB2的相对含量.超重力条件下,反应物颗粒接触更加充分,碰撞更加频繁,因而晶粒形态发育更加完整,生成规则的多面体.
参考文献
| [1] | 孙康 .[J].钒钛,1995,5:22. |
| [2] | Matsushita J;Suzuki T;Sano A .[J].Journal of the Ceramic Society of Japan,1992,100:219. |
| [3] | Zhu Chuncheng;Qu Wei;Zhang Xinhong et al.[J].Materials Guide Report,2003,17(01):48. |
| [4] | Li Jianlin;Li Fei;Hu Keao et al.[J].Journal of the European Ceramic Society,2001,21(02):2829. |
| [5] | Kustas F.;Mishra B.;Zhou J. .Fabrication and characterization of TiB2/TiC and tungsten co-sputtered wear coatings[J].Surface & Coatings Technology,2002(1):25-30. |
| [6] | Wang H Y;Jiang Q C;Zhao Y Q et al.[J].Material Science and Engineering,2004,372(03):109. |
| [7] | Bhaumik SK.;Singh AK.;Upadhyaya GS.;Divakar C. .Synthesis and sintering of TiB2 and TiB2-TiC composite under high pressure[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):275-281. |
| [8] | Klinger L.;Horvitz D.;Gotman I. .In situ processing of TiB2/TiC ceramic composites by thermal explosion under pressure: experimental study and modeling[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1):92-99. |
| [9] | Lee JW.;Munir ZA.;Ohyanagi M. .Dense nanocrystalline TiB2-TiC composites formed by field activation from high-energy ball milled reactants[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):221-227. |
| [10] | Lee Kitty W;Chen Yu-Hsia;Chung Yip-Wah et al.[J].Surface and Coatings Technology,2004,177/178:591. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%