在4Cr13不锈钢表面采用多弧离子镀沉积TiAlN薄膜,采用磁控溅射法和多弧离子镀在4Cr13表面分别沉积掺杂Cr和Cr、Ni的TiAlN薄膜,采用电化学工作站对其进行电化学腐蚀性能测试.结果表明:在l mol/L的H2SO4溶液中,同时掺杂Cr、Ni的TiAlN薄膜的耐腐蚀性是TiAlN薄膜的4.1倍,是掺杂Cr的TiAlN薄膜的1.3倍;在3％的NaOH溶液中,同时掺杂Cr、Ni的TiAlN薄膜的耐腐蚀性是TiAlN薄膜的3倍,是掺杂Cr的TiAlN薄膜的2倍;在3.5％的NaCl溶液中,同时掺杂Cr、Ni的TiAlN薄膜的耐腐蚀性是TiAlN薄膜的11.4倍,是掺杂Cr的TiAlN薄膜的1.3倍.
参考文献
| [1] | Paul H. Mayrhofer;Christian Mitterer;Lars Hultman;Helmut Clemens.Microstructural design of hard coatings[J].Progress in materials science,20068(8):1032-1114. |
| [2] | S. Niyomsoan;W. Grant;D.L. Olson.Variation of color in titanium and zirconium nitride decorative thin films[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,20021/2(1/2):187-200. |
| [3] | Ma LW;Cairney JM;Hoffman MJ;Munroe PR.Deformation and fracture of TiN and TiAlN coatings on a steel substrate during nanoindentation[J].Surface & Coatings Technology,200611(11):3518-3526. |
| [4] | Kamiya S;Nagasawa H;Yamanobe K;Saka M.A comparative study of the mechanical strength of chemical vapor-deposited diamond and physical vapor-deposited hard coatings[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,20051(1):123-131. |
| [5] | 罗宏.SUS304ss包埋粉末渗铝的耐蚀性能[J].中国腐蚀与防护学报,2009(05):344-348. |
| [6] | 隗晓云 .反应溅射形成氮化钛复合渗镀层耐磨耐腐蚀性能的研究[D].太原理工大学,2006. |
| [7] | 林绿波;戴品强;林兰芳;廖耀祥.纳米晶Co-Ni-Fe合金镀层在3.5％NaCl溶液中的腐蚀特性[J].稀有金属材料与工程,2012(5):851-856. |
| [8] | 高原;韦文竹;袁琳;陈选楠;王成磊;陆小会;张焱;吴炜钦;张光耀.等离子铬镍共渗层与氮化钛薄膜的耐蚀性[J].材料热处理学报,2013(z1):129-134. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%