在参考文献的基础上,成功地合成出性能优良的卡波姆产品.通过扫描电镜(SEN),首次观察了卡波姆水凝胶的微观结构,并考察了交联剂用量对水凝胶交联密度的影响.结果表明,随着交联剂用量的增加,卡波姆的交联密度逐渐增大,当交联剂用量达到2.0％时,卡波姆不能在水中完全溶胀.
参考文献
| [1] | 张方涛,罗钟瑜,修玉英.聚氨酯缔合增稠剂增稠机理及增稠效果研究进展[J].合成材料老化与应用,2009(02):50-54. |
| [2] | 赖宝林,王利胜,张升,田瑶.中药凝胶剂的研究进展[J].中药新药与临床药理,2010(02):211-封3. |
| [3] | 薛铁中,华慢,袁立新.卡波树脂在化妆品中的应用[J].日用化学品科学,2009(11):39-42. |
| [4] | 卢毅,张彤,陶建生.卡波姆在药剂学中的应用[J].中国医药工业杂志,2007(06):457-460. |
| [5] | Barry B W;Meyer M C .The rheological properties of carbopol gels I.Continuous shear and creep properties of carbopol gels[J].International Journal of Pharmaceutics,1979,2(01):1-25. |
| [6] | Dolan M M;Steelman R L;Tumilowicz R R .Carbopol 934:An improved suspending agent for insoluble test compounds[J].Toxicology and Applied Pharmacology,1960,2(03):331-337. |
| [7] | Berney B M;Deasy P B .Evaluation of carbopol 934 as a suspending agent for sulphaoimidine suspensions[J].International Journal of Pharmaceutics,1979,3(2-3):73-80. |
| [8] | Pérez-Marcos B;Martínez-Pacheco R;GómezAmoza J L et al.Interlot variability of carbomer 934[J].International Journal of Pharmaceutics,1993,100(1-3):207-212. |
| [9] | C. Gomez;B. Derakhshandeh;S.G. Hatzikiriakos;C.P.J. Bennington .Carbopol as a model fluid for studying mixing of pulp fibre suspensions[J].Chemical Engineering Science,2010(3):1288-1295. |
| [10] | Sharmin N;Elias-A1-Mamun M;Jalil R .A Novel Method to Study the Effect of pH and Excipients on Water Uptake and Swelling Behaviour of Carbopol Polymers[J].Bangladesh Pharmaceutical Journal,2010,13(02):1-7. |
| [11] | 王一龙,毕彩丰,赵宇,王强,申云霞.卡波树脂的合成及性能研究[J].中国海洋大学学报（自然科学版）,2010(09):105-108,122. |
| [12] | 连佳芳,郝勇,张林祺.卡波姆及其在凝胶剂中的应用研究进展[J].白求恩军医学院学报,2008(03):162-163. |
| [13] | 华慢,张若昕,袁立新.卡波树脂沉淀聚合法的合成及其应用性能[J].日用化学品科学,2007(10):18-22. |
| [14] | 刘德荣,李春霞,彭炜.合成卡波姆新工艺研究[J].化工生产与技术,2007(04):23-26. |
| [15] | 张宇,叶华,赵建青.耐盐性高吸水树脂的研究进展[J].合成材料老化与应用,2003(03):42-47. |
| [16] | Jeong Min Jin;Jung Min Lee;Min Hye Ha .Highly crosslinked poly(glycidyl methacrylate-co-divinyl benzene) particles by precipitation polymerization[J].Polymer: The International Journal for the Science and Technology of Polymers,2007(11):3107-3115. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%