EFFECT OF Zr ADDITION TO Ti-KILLED STEEL ON INCLUSION FORMATION AND MICROSTRUCTURAL EVOLUTION IN WELDING INDUCED COARSE-GRAINED HEAT AFFECTED ZONE

金属学报(英文版), 2008, 21(3): 220-226.

^1, , ^2, , ^3, , ^4, , ^5, , ^6,

1.Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081, China

2.Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081, China

3.Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081, China

4.Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081, China

5.School of Materials Science and Engineering, Shanghai Jiaotong University, Shanghai 200030, China

6.School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China

基金项目: New Generation Project of Cycled Iron and Steel(2006BAE03A15)

EFFECT OF Zr ADDITION TO Ti-KILLED STEEL ON INCLUSION FORMATION AND MICROSTRUCTURAL EVOLUTION IN WELDING INDUCED COARSE-GRAINED HEAT AFFECTED ZONE

F.Chai ^1, , C.F.Yang ^2, , H.Su ^3, , Y.Q.Zhang ^4, , Z.Xu ^5, , Y.H.Yang ^6,

1.Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081, China

2.Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081, China

3.Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081, China

4.Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081, China

5.School of Materials Science and Engineering, Shanghai Jiaotong University, Shanghai 200030, China

6.School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China

Keywords： Nonmetallic inclusions

Effects of Zirconium on the chemical component and size distribution of Ti-bearing inclusions, favored the grain refinement of the welding induced, coarse-grained heat affected zone (CGHAZ) with enhanced impact toughness in Ti-killed steels, which were examined based on experimental observations and thermodynamic calculations.It indicated that the chemical constituents of inclusions gradually varied from the TiO oxide to the Ti-O+Zr-O compound oxide and a single phase of the ZrO2 oxide,as the Zr content increased from zero to 0.0100%. A trace of Zr (0.0030%-0.0080%,depending on the oxygen content in liquid steel) provided a large amount of nucleating core for Ti oxide because of the larger specific density of ZrO2 oxide, and produced a small size distribution of the inclusions favorable for aeieular ferrite transformation with a high nucleation rate in the CGHAZ, and a high volume fraction of aeicular ferrite was obtained in the CGHAZ, with enhanced impact toughness. Otherwise, a high content of Zr (～0.0100%) produced a single phase ZrO2, which was impotent to nucleate acicular ferrite, and a microstructure composed of ferrite side plate and grain boundary ferrite developed in the CGHAZ. The experimental results were confirmed by thermodynamic calculations.

参考文献

[1]	H Homma;S Okita;S Matsuda;K.Yamamoto .[J].Welding Journal,1987,66:301.
[2]	S Mizoguchi.[A].Pohang,Corea,2002
[3]	G M Evans .[J].Welding Research,1995,8:249s.
[4]	T Yukio;S Naoki;T Takeshi .[J].ISIJ International,1994,10:829.
[5]	J.-H. SHIM;Y. W. CHO .NUCLEATION OF INTRAGRANULAR FERRITE AT Ti2O3 PARTICLE IN LOW CARBON STEEL[J].Acta materialia,1999(9):2751-2760.
[6]	S Takashi;W Masamitsu;U Yoshiyuki .[J].ISIJ International,1992,1:169.
[7]	A. B. FOX;M. E. VALDEZ;J. GISBY .Dissolution of ZrO_2, Al_2O_3, MgO and MgAl_2O_4 Particles in a B_2O_3 Containing Commercial Fluoride-free Mould Slag[J].ISIJ International,2004(5):836-845.
[8]	J S Yun;J H Shim;Y W Cho .[J].Acta Materialia,2003,51:1593.
[9]	K S Oh.[A].Pohang,Corea,2002
[10]	J L Lee .[J].Acta Materialia,1994,10:3291.
[11]	K Jae;H J Sim;B Y Sang .[J].ISIJ International,2000,12:1260.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

EFFECT OF Zr ADDITION TO Ti-KILLED STEEL ON INCLUSION FORMATION AND MICROSTRUCTURAL EVOLUTION IN WELDING INDUCED COARSE-GRAINED HEAT AFFECTED ZONE

参考文献