在离子氮化前后的H13钢表面沉积了CrAlN薄膜,研究了其在质量分数为3.5%的NaCl溶液中的耐腐蚀性,并用场发射扫描电镜观察了薄膜腐蚀前后的表面形貌。结果表明：H13钢基体表面沉积CrAlN薄膜后的耐腐蚀性能显著提高;经离子氮化和表面沉积CrAlN薄膜复合处理后,耐腐蚀性进一步提高,试验后表面没有出现明显的腐蚀坑及膜层脱落。
CrAlN thin films was deposited on H13 steel surface before and after ionitriding,the corrosion resistance of CrAlN thin films in 3.5wt% NaCl solution was studied,and the surface morphology of thin films before and after corrosion was observed by field emission scanning electron microscopy.The results show that the corrosion resistance of H13 steel after depositing CrAlN thin films increased remarkably.The complex process of ionitriding and depositing CrAlN thin films made corrosion resistance of H13 steel increase further,and obvious corrosion pits and films desquamation had not found on H13 steel surface after polarization test.
参考文献
| [1] | Harish C. Barshilia;B. Deepthi;N. Selvakumar;Anjana Jain;K.S. Rajam .Nanolayered multilayer coatings of CrN/CrAlN prepared by reactive DC magnetron sputtering[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2007(11):5076-5083. |
| [2] | J. Walkowicz;J. Smolik;J. Tacikowski .Optimization of nitrided case structure in composite layers created by duplex treatment on the basis of PVD coating adhesion measurement[J].Surface & Coatings Technology,1999(0):370-379. |
| [3] | Masao YAKUSHIJI;Masaru IKENAGA;Yoshiro ISHII .SURFACE MODIFICATION BY DUPLEX PROCESS CONSISTED OF RADICAL NITRIDING AND PVD[J].Materials Science Forum,2003(Pt.3):2611-2616. |
| [4] | J. C. A. Batista;M. C. Joseph;C. Godoy;A. Matthews .Micro-abrasion wear testing of PVD TiN coatings on untreated and plasma nitrided AISI H13 steel[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2001(10/11):971-979. |
| [5] | Ma SL.;Xu KW.;Li YH. .The composite of nitrided steel of H13 and TiN coatings by plasma duplex treatment and the effect of pre-nitriding[J].Surface & Coatings Technology,2001(2/3):116-121. |
| [6] | Scheerer, H;Floche, H;Broszeit, E;Schramm, B;Abele, E;Berger, C .Effects of the chromium to aluminum content on the tribology in dry machining using (CrAI)N coated tools[J].Surface & Coatings Technology,2005(1/4):203-207. |
| [7] | Brizuela, M;Garcia-Luis, A;Braceras, I;Onate, JI;Sanchez-Lopez, JC;Martinez-Martinez, D;Lopez-Cartes, C;Fernandez, A .Magnetron sputtering of Cr(AI)N coatings: Mechanical and tribological study[J].Surface & Coatings Technology,2005(1/4):192-197. |
| [8] | Romero J;Gomez MA;Esteve J;Montala F;Carreras L;Grifol M;Lousa A .CrAlN coatings deposited by cathodic arc evaporation at different substrate bias[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2006(1):113-117. |
| [9] | P. J. Kelly;R. D. Arnell .The influence of magnetron configuration on ion current density and deposition rate in a dual unbalanced magnetron sputtering system[J].Surface & Coatings Technology,1998(1/3):317-322. |
| [10] | Gannon PE;Tripp CT;Knospe AK;Ramana CV;Deibert M;Smith RJ;Gorokhovsky V;Shutthanandan V;Gelles D .High-temperature oxidation resistance and surface electrical conductivity of stainless steels with filtered arc Cr-Al-N multilayer and/or superlattice coatings[J].Surface & Coatings Technology,2004(0):55-61. |
| [11] | L. Cunha;M. Andritschky;L. Rebouta;K. Pischow .Corrosion of CrN and TiAlN coatings in chloride-containing atmospheres[J].Surface & Coatings Technology,1999(0):1152-1160. |
| [12] | Mendibide, C;Steyer, P;Millet, JP .Formation of a serniconductive surface film on nanomultilayered TiN/CrN coatings and its correlation with corrosion protection of steel[J].Surface & Coatings Technology,2005(1/4):109-112. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%