采用气-渣平衡法,用铂坩埚作反应容器,CO-CO2-SO2-N2混合气体提供体系的氧分压和硫分压,测定了一定炉渣成分,不同温度和气氛条件下CaO-SiO2一A12O3一MgO-FetO五元渣系的硫容量.研究得出,对于一定成分组成的CaO-SiO2-A12O3-MgO-FetO五元渣系,当气体流量不变时,硫容量随炉渣温度的升高而减小;当温度一定时,硫容量随体系氧分压增大而增大.
参考文献
| [1] | Delport H M W .The Corex Process[J].Ironmaking and Steelmaking,1992,19(03):183. |
| [2] | 杜鹤桂.浦项钢铁公司的炼铁生产[J].国外钢铁,1996(05):1. |
| [3] | Lemperce M;Maschlake W;Andvoest-Alpin D.Corex法的现在和未来[J].国外钢铁,1994(05):7. |
| [4] | 徐国群.Auslron炼铁新技术[J].上海金属,2003(01):30-35. |
| [5] | Wagner C;Elliott J F;John W.Physical Chemistry of SteelMaking[M].New York:Academic Press,Inc,1999:71. |
| [6] | 杜挺,吴夜明,曹明艳.含碳球团-铁浴熔融还原炼铁法与COREX法的能耗比较[J].钢铁研究学报,1999(03):71-74. |
| [7] | 郭占成 .铁水在熔融还原炉内脱硫精炼[J].钢铁,1992,27(12):11. |
| [8] | Wang C L;Lu Q;Zhang S H et al.Study on Sulphide Capacity of CaO-SiO2-Al2O3-MgO-FeO Slags[J].Journal of University of Science and Technology Bering,2006,13(03):213. |
| [9] | Seo J D;Kim S H .The Sulphide Capacity of CaO-SiO2Al2O3-MgO(-FeO)Smelting Reduction Slags[J].Steel Research International,1999,70(06):203. |
| [10] | 王常珍.冶金物理化学研究方法[M].北京:冶金工业出版社,2002:188. |
| [11] | 李洪桂.冶金原理[M].北京:科学出版社,2005:109. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%