孔结构是影响砂浆或混凝土性能的重要参数.通过压汞法研究了橡胶颗粒对砂浆孔隙率及孔径分布的影响规律,分析了橡胶颗粒对砂浆孔结构的影响机理.结果表明,随橡胶颗粒含量增加,橡胶砂浆最可几孔径增加,总孔隙率增加,其中大孔(D>1000 nm)含量增加最为明显,而凝胶孔(D<10 nm)含量变化不大.橡胶表面与水的接触角为99.5.,说明其具有憎水性,同时由于橡胶颗粒表面存在着大量凹坑,水在毛细管作用下无法充满橡胶颗粒表面凹坑,导致橡胶颗粒与水泥基体界面处存在大量孔径较大的孔隙.
参考文献
| [1] | Malek K. Batayneh;Iqbal Marie;Ibrahim Asi .Promoting the use of crumb rubber concrete in developing countries[J].Waste Management,2008(11):2171-2176. |
| [2] | Erhan Guneyisi;Mehmet Gesoglu;Turan Ozturan .Properties of rubberized concretes containing silica fume[J].Cement and Concrete Research,2004(12):2309-2317. |
| [3] | Ganjian E;Khorami M;Maghsoudi A A .Scrap tyre rubber replacement for aggregate and filler in concrete[J].Construction and Building Materials,2008,23(05):1828. |
| [4] | N. Segre;I. Joekes .Use of tire rubber particles as addition to cement paste[J].Cement and Concrete Research,2000(9):1421-1425. |
| [5] | D.G. Snelson;J.M. Kinuthia;P.A. Davies .Sustainable construction: Composite use of tyres and ash in concrete[J].Waste Management,2009(1):360-367. |
| [6] | 朱涵,刘春生,张永明,李志国.橡胶集料掺量对混凝土压弯性能的影响[J].天津大学学报,2007(07):761-765. |
| [7] | 亢景付,张振利,韩春翠.等强条件下橡胶粉对碾压混凝土强度与变形性能的影响[J].复合材料学报,2009(02):155-159. |
| [8] | 刘锋,张文杰,何东明,李丽娟.橡胶粉-纤维改性高强混凝土的高温性能[J].建筑材料学报,2011(01):124-131. |
| [9] | F. Hernandez-Olivares;G. Barluenga .Fire performance of recycled rubber-filled high-strength concrete[J].Cement and Concrete Research,2004(1):109-117. |
| [10] | Benazzouk A;Douzane O;Mezre K .Thermal conductivity of cement composites containing rubber waste particles:Experimental study and modeling[J].Construction and Building Materials,2008,22(04):73. |
| [11] | 胡鹏,朱涵.掺橡胶细粒混凝土的渗透性与微观结构[J].混凝土与水泥制品,2007(02):4-6. |
| [12] | 张亚梅 .橡胶粉对混凝土在水和NaCl溶液中抗冻性的影响[J].东南大学学报(自然科学版),2006,36(zⅡ):248. |
| [13] | 杨林虎,朱涵,张亚梅.橡胶集料对水泥砂浆孔结构的影响[J].天津大学学报,2011(12):1083-1087. |
| [14] | Rafat Siddique;Tarun R. Naik .Properties of concrete containing scrap-tire rubber--an overview[J].Waste Management,2004(6):563-569. |
| [15] | 肖焕秀,敖宁建,谭海生.聚硅氧烷对天然橡胶表面耐溶剂性的影响[J].弹性体,2007(06):1-4. |
| [16] | 刘春生;朱涵.橡胶集料表面特性对混凝土渗透性的影响[J].商品混凝土,2009(12):41. |
| [17] | 吴中伟;廉慧珍.高性能混凝土[M].北京:中国铁道出版社,1999 |
| [18] | 张海波,管学茂,刘小星,李飞.废旧橡胶颗粒对混凝土强度的影响及界面分析[J].材料导报,2009(08):65-67. |
| [19] | 史新亮 .废旧轮胎橡胶路面混凝土性能研究[D].焦作:河南理工大学,2008. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%