研制了一种新型镁合金的无Cr阳极氧化配方,对镁合金进行 阳极化处理.溶液的主要成分为NaOH、NaSiF6和有机添加剂.XRD、SEM、XPS测试结果表明 ,氧化膜主要由MgO、MgAl2O4和2Al2O3·2SiO2·H2O组成.35%NaCl水溶 液动电位极化结果说明,氧化膜有良好耐点蚀性能.合金中Si、Al元素的氧化弥补了Mg氧化 时的体积收缩,氧化膜无裂纹,为其耐点蚀提供了条件.阳极化后Al、Si元素在表面均匀分 布,是氧化膜具有良好保护作用的原因之一.

A suitable mixture without chromium is developed for protection of mag nesium alloys by treatment with the anodic oxidation.The aqueous solution is co mposed of NaOH、Na2SiF6 and an organic additive.The potentiodynamic polariza tio n measurement showed that the film had outstanding protective ability in 3.5% Na Cl solution.The morphology and component of the anodic oxidation film have been analysed by SEM,XRD,XPS and EPMA respectively.XRD and EPMA analysis revealed that the film was made of MgO、MgAl2O4 and 2Al2O3·2SiO2·H2O.Si and Al oxides make up the volume shrinkage of magnesium oxides,so that the film has no crack which provides a good condition against pitting.And the even dispersio ns of Si and Al in the film is another factor that the film has better protectio n.

参考文献

[1]
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%