Combustion catalyst La0.8Sr0.2CoO3 (LSC) is expected to possess relatively high activity for the oxidation of carbon monoxide and many hydrocarbons. If γ-Al2O3 is used as its support, cobalt ions can easily react with γ-Al2O3 at not very high temperature to form spinel CoAl2O4 or spinel-like, which decreases the activity of the combustion catalyst. In this paper, MgAl2O4 and CaAl2O4 were pre-coated on γ-Al2O3 by impregnation respectively, which formed compound support for LSC. It is shown that, when MgAl2O4 layer is covered on the surface of MgAl2O4 by impregnation, the entering of cobalt ions into γ-Al2O3 lattice is restrained, then LSC formed on the surface of MgAl2O4, which leads to a good catalytic activity of xylene complete oxidation. But the layer of MgAl2O4 should be thick enough to reach 30% (mass fraction) MgO in the support due to large size particle of MgAl2O4 crystalline. If polyvinyl alcohol (PVA) is added into the impregnation solution adequately, MgAl2O4 particles formed on the surface of γ-Al2O3 are getting smaller, and less amount of MgAl2O4 is needed to cover up the surface of γ-Al2O3. If CaAl2O4 layer substituted for MgAl2O4, more closed cover is obtained in virtue of fine particles of CaAl2O4. The activity examination shows that smaller particles of MgAl2O4 or CaAl2O4 can be more effective to hinder cobalt ions entering the lattice of γ-Al2O3, and better activities will be obtained.
参考文献
| [1] | Voorhoeve R J H.Advanced Materials in Catalysis[M].New York:Academic Press,1977 |
| [2] | Libby W F .Promising catalyst for auto exhaust[J].Science,1971,171:499. |
| [3] | Pedersen L A;Libby W F .Unseparated rare earth cobalt oxides auto exhaust catalysts[J].SCIENCE,1972,172:1355. |
| [4] | Voorhoeve R J H;Remeika J P;Johnson D W .Rare-earth manganites:catalysts with low ammonia yield in the reduction of nitrogen oxides[J].Science,1973,180:62. |
| [5] | Wu Shanliang;Zhang Zhigang;Huang Guozhang .Studies of CM-type series rare earth catalyst for catalytic combustion[J].Environmental Chemistry(in Chin),1989,8(01):1. |
| [6] | Wu Bin;Shen Yuenian;Hun Ruisheng .Studies on the pre-coated cordierite support and corresponding properties[J].Acta Scientiarum Naturalium Universitatis Neimongol(in Chin),2000,31(04):398. |
| [7] | Nudel J N;Umansky B S;Lombardo E A .Bulk, Surface and Catalytic characterization of the Co3O4-La2O3-Al2O3 system[J].Applied Catalysis,1987,31:275. |
| [8] | Meng Ming;Lin Peiyan;Fu Yilu .Co/γ-Al2O3 catalysts for nitric oxide selective reduction by ethylene[J].催化学报,1998,19:70. |
| [9] | Jia Meilin;Shen Yuenian;Qin Feili .Effects of support on the performance of combustion catalyst La0.8Sr0.2CoO3/γ-Al2O3[J].Journal of Molecular Catalysis(in Chinese),2000,14:265. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%