以硫酸铝为铝源,氨水为沉淀剂,采用pH摆动法辅以共沸蒸馏处理制备γ-Al2O3前驱体,经550℃焙烧得到了γ-Al2O3.采用XRD、BET法、SEM、TEM等手段对γ-A12O3进行表征.pH摆动法在反应温度80℃,pH摆动3次,不需额外老化条件制备的γ-A12O3比表面积、平均孔径、孔容最大,样品无规则形貌;辅以共沸蒸馏处理可制备分散性良好、粒径均匀的介孔纤维状纳米γ-Al2O3,平均粒径宽5nm,长40-60nm,与PH摆动法制备样品相比,比表面积相当,高达327m2/g,孔径、孔容提高很大,达到16.04nm和1.31cm3/g.
参考文献
| [1] | Zhang Z R;Hicks R W;Pauly T R et al.[J].Journal of the American Chemical Society,2002,124:1592-1593. |
| [2] | Faria FP.;Santos PS.;Santos HS. .Spatial arrangement of fibrils in concentrated aqueous sols of fibrillar pseudoboehmite[J].Materials Chemistry and Physics,2002(3):267-273. |
| [3] | Tanaka K;Imai T;Murakami T et al.[J].Chemistry Letters,2002,31:110-111. |
| [4] | 杜明仙,翟效珍,李源,李林东,朱华青,谭长瑜.高比表面积窄孔分布氧化铝的制备Ⅰ. 沉淀条件的影响[J].催化学报,2002(05):465-468. |
| [5] | Kaliszewski M S;Heuer A H .[J].Journal of the American Ceramic Society,1990,73(06):1504-1509. |
| [6] | Cai WQ;Li HQ;Zhang Y .Azeotropic distillation-assisted preparation of macro-mesostructured gamma-Al2O3 nanofibres of crumpled sheet-like morphology[J].Materials Chemistry and Physics,2006(1):136-139. |
| [7] | 包建国,杨运泉,王威燕,王玉林,刘文英.共沸蒸馏-均匀沉淀法制备大孔体积和孔径的介孔纳米γ-Al2O3[J].石油化工,2009(08):839-844. |
| [8] | 徐如人;庞文琴.分子筛与多孔材料化学[M].北京:科学出版社,2004 |
| [9] | Cějka J;(Z)ilkováN;Rothousky J et al.[J].Langmuir,2004,20:7532-7539. |
| [10] | 宋晓岚,邱冠周,王海波,吴雪兰,曲选辉.高纯活性纳米γ型氧化铝的化学沉淀法合成及其性能表征[J].材料导报,2004(08):64-67. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%