The oxidation behavior of alloy 690 exposed to high-temperature and high-pressure steam and water at 280℃ for 1 h was investigated by scanning electron microscopy （SEM）, atomic force microscopy （AFM） and X-ray photoelectron spectroscopy （XPS）. In high-temperature and high-pressure steam, the oxide film is composed of an outermost Ni-rich hydroxides layer, an intermediate layer of hydroxides and oxides enriched in Cr, an inner oxide layer. The film formed in high-temperature water is similar to that in steam, except for missing the Ni-rich hydroxides layer. Samples with different surface finishes （electropolished, mechanically polished, ground, and as-received） were prepared for comparison. A general increase of the oxide thickness with the degree of surface roughness is observed. The equivalent oxide thicknesses lie in the range of 100-200 nm for the as-received samples, 150-250 nm for the samples ground to 400# and 10-20 nm for the samples ground to 1500#, mechanically polished, and electropolished.
参考文献
| [1] | L. Marchetti;S. Perrin;Y. Wouters;F. Martin;M. Pijolat .Photoelectrochemical study of nickel base alloys oxide films formed at high temperature and high pressure water[J].Electrochimica Acta,2010(19):5384-5392. |
| [2] | A. Machet;A. Galtayries;S. Zanna;L. Klein;V. Maurice;P. Jolivet;M. Foucault;P. Combrade;P. Scott;P. Marcus .XPS and STM study of the growth and structure of passive films in high temperature water on a nickel-base alloy[J].Electrochimica Acta,2004(22/23):3957-3964. |
| [3] | R. Mahfouz;F.J. Cadete Santos Aires;A. Brenier;B. Jacquier;J.C. Bertolini .Synthesis And Physico-chemical Characteristics Of Nanosized Particles Produced By Laser Ablation Of A Nickel Target In Water[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2008(16):5181-5190. |
| [4] | T. SUNDARARAJAN;S. KURODA;K. NISHIDA .Behaviour of Mn and Si in the Spray Powders during Steam Oxidation of Ni-Cr Thermal Spray Coatings[J].ISIJ International,2004(1):139-144. |
| [5] | G.T. Burstein;P.C. Pistohus .Surface Roughness and the Metastable Pitting of Stainless Steel in Chloride Solutions[J].Corrosion: The Journal of Science and Engineering,1995(5):380-385. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%