为了探究纯铁在天然海水中的腐蚀机理以及流速对其腐蚀行为的影响,进而对铁合金腐蚀研究提供理论基础,采用自行制造的水槽式流体流动装置,模拟流动海水对纯铁的腐蚀状况,利用电化学测试手段(自腐蚀电位监测,动电位极化)并结合表面与截面形貌分析,研究了纯铁在静止和选取流速(0.2,0.3,0.4 m/s)下的海水中的腐蚀行为.结果表明:纯铁在流动海水中的耐蚀性比静止时差,且流速越大耐蚀性越差,其腐蚀过程仍主要受阴极氧扩散控制;纯铁在海水中的自腐蚀电位随流速的提高而负移.纯铁在静止海水中的腐蚀产生突起状形貌,在流动海水中腐蚀产生具有明显方向性的腐蚀坑.
The corrosion mechanism of pure iron in natural seawater and effect of flowing velocity on the corrosion be-havior were investigated, aiming at providing theoretical basis for the research of corrosion of ferroalloys. Thus electrochemical tests such as monitoring of potential electrochemical corrosion and measuring of kinetic potential polarization were conducted on a sink-like fluid flowing device to investigate the corrosion behavior of pure iron in still seawater and seawater flowing at a velocity of 0. 2, 0. 3 m/s, and 0. 4 m/s. The morphologies of the corroded surfaces and crosssections were observed using a scanning elec-tron microscope. Results show that pure iron in the flowing sea-water had poorer corrosion resistance than that in still seawater, and its corrosion resistance became increasingly worsened with in-creasing flowing velocity. At the same time, the corrosion process of pure iron in seawater was still mainly controlled by diffusion of oxygen at cathode. Moreover, the corrosion potential of pure iron shifted negatively as the flowing velocity rose. And protrusions were formed on the corroded surfaco of pure iron in still seawater, while corrosion pits with obvious orientation were formed on the corroded surface in flowing seawater.
参考文献
| [1] | 潘牧;罗志平 .材料的冲蚀问题[J].材料科学与工程,1999,17(03):92-96. |
| [2] | 杨武;顾睿祥;肖景光.金属的局部腐蚀[M].北京:化学工业出版社,1995:299-302. |
| [3] | 江旭,柳伟,路民旭.钢铁海洋大气腐蚀试验方法的研究进展[J].腐蚀科学与防护技术,2007(04):282-286. |
| [4] | Shalaby H M;Attari S;Riad W T et al.Erosion-corrosion behavior of some cast alloys in seawater[J].Corrosion,1992,48(03):206-217. |
| [5] | 田兴玲,林玉珍,刘景军,雍兴跃.碳钢在液/固双相管流中的磨损腐蚀机理研究[J].北京化工大学学报(自然科学版),2003(05):40-43. |
| [6] | 刘景军,林玉珍,雍兴跃,李效玉.铁素体/奥氏体双相钢在旋转单相流体中腐蚀的数值模拟[J].中国腐蚀与防护学报,2003(05):290-294. |
| [7] | Chen T Y;Moccari A A .Development of controlled hydrodynamic techniques for corrosion testing[J].Corrosion,1992,48(03):239-255. |
| [8] | Efird K D;Wright E J;Boros J A et al.Experimental correlation of steel corrosion in pipe flow with jet impingement and rotating cylinder lab tests[J].Corrosion,1993,49(12):992-1 003. |
| [9] | 王曰义.金属的典型腐蚀形貌[J].装备环境工程,2006(04):31-37. |
| [10] | 梁成浩.金属腐蚀学导论[M].北京:机械工业出版社,1988:125-126. |
| [11] | 郑玉贵,姚治铭,柯伟.流体力学因素对冲刷腐蚀的影响机制[J].腐蚀科学与防护技术,2000(01):36-40. |
| [12] | 夏兰廷,韦华,朱宏喜.常用铸铁材料海水腐蚀行为的研究[J].中国腐蚀与防护学报,2003(02):99-102. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%