采用柠檬酸溶胶凝胶法制备了稀土W型六角铁氧体Ba0.8La0.2Co2Fe16O27粉晶,用DSC-TGA、FT-IR、XRD、SEM分析了样品的形成过程、微观形貌、粒径和晶体结构,根据微波矢量网络分析仪测试的样品在2～18GHz微波频率范围的电磁参数计算了电磁损耗角正切及微波反射率.研究结果表明, 煅烧2h能得到单一的W型相Ba0.8La0.2Co2Fe16O27 ;晶粒为六角块状结构,大小均为200nm左右;Ba0.8La0.2Co2Fe16O27样品厚度为1.9mm时,12GHz位置处吸收峰为16.2dB,10dB频宽为4.0GHz;微波吸收主要由磁损耗引起.
参考文献
| [1] | Ghasemi A;Liu X X;Morisako A .[J].Journal of Magnetism and Magnetic Materials,2007,316(02):1105-1108. |
| [2] | Yi Yang;Baoshan Zhang;Weidong Xu .Microwave absorption studies of W-hexaferrite prepared by co-precipitation/mechanical milling[J].Journal of Magnetism and Magnetic Materials,2003(2):119-122. |
| [3] | Wang L X;Huang Q;Mu L et al.[J].Journal of Rare Earths,2007,25(z2):216-219. |
| [4] | 王海泉,陈秀琴.吸波材料的研究进展[J].材料导报,2003(z1):170-173. |
| [5] | 刘清玲.稀土元素在光、电、磁方面的研究应用进展[J].河南师范大学学报（自然科学版）,2003(04):71-74. |
| [6] | Chen N;Mu G H;Pan X F et al.[J].Materials Science and Engineering B:Solid State Materials for Advanced Technology,2007,139(2-3):256-260. |
| [7] | Miura K;Masuda M;Itoh M et al.[J].Journal of Alloys and Compounds,2006,408-412:1017-1021. |
| [8] | 廖绍彬.铁磁学[M].北京:科学出版社,1988 |
| [9] | 云月厚,靳杰,张伟,李国栋.化学共沉淀法制备的BaNiZnCexFe16-xO27超微粉末的微波吸收特性[J].稀土,2006(05):76-79. |
| [10] | 李红英,施伟光,甘树才.稀土六方Z型铁氧体Ba3-xLaxCo2Fe24O41的合成及电磁性能与吸波特性[J].吉林大学学报（工学版）,2006(06):856-860. |
| [11] | 钟文定.铁磁学[M].北京:科学出版社,1998 |
| [12] | 甘树才,李红英,孟健,洪广言.溶胶-凝胶法合成稀土Z型铁氧体Ba3-xLaxCo2Fe24O41与表征[J].中国稀土学报,2004(06):751-754. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%