对新型2198铝锂合金进行Alodine 1200S化学转化处理。采用极化曲线和电化学阻抗谱研究不同转化时间处理前后该合金在3．5％NaCl溶液中的腐蚀破坏过程。根据铬酸盐化学转化处理后铝锂合金的电化学阻抗谱特征，建立与之相应的电化学等效电路模型，并分析了化学转化膜的成膜机理。结果表明，化学转化处理促使铝锂合金的自腐蚀电位和击穿电位正移。化学转化处理的合金Nyquist图低频容抗半径和Bode图阻抗模值大小随化学转化时间延长先增大后减小，出现极值。转化时间为1min 30S时容抗弧和感抗弧半径最大，阻抗模值最大，阻抗相位角最接近-90°。转化膜表面可能吸附部分的K3[Fe（CN）6]促进剂和游离的六价铬，在NaCl溶液中浸泡时，可能发生局部表面的吸脱附和扩散。
The corrosion properties of 2198 Al-Li alloy and chromate conversion coated 2198 Al-Li alloys with different treating times were studied by polarization curves and electrochemical impedance spectroscopy (EIS) in 3. 5% NaCl solution. According to the characteristics of EIS, the electrochemical equivalent circuit was established. The formation mechanism of chromate conversion coating on the alloy was further analyzed. The results showed that Ecorr and Eb of the alloy shifted positively after chromate conversion coating treatment. The radius of capacitive arcs in Nyquist plot increased first and then decreased. The radius of capacitive arcs became the maximum when the treating time was 1 min and 30 second. Under the same condition, the modulus of corrosion resistance became the maximum, and the phase angle of corrosion resistance was the closest to --90°. Few amounts of K3 [Fe(CN)6 ] accelerator and free Cr(Ⅵ) species were adsorbed on the coating surface, and parts of them desorbed and diffused during the immersion process.
参考文献
| [1] | 峻峰.AirwareTM2198合金：“猎鹰”家族航空飞行器的支柱[J].世界有色金属,2011(06):66-68. |
| [2] | Conde A.;de Damborenea J. .Electrochemical modelling of exfoliation corrosion behaviour of 8090 alloy[J].Electrochimica Acta,1998(8):849-860. |
| [3] | 潘清林,李运春,梁文杰,何运斌,周迎春,路聪阁,刘晓艳.预变形对新型含钪Al-Cu-Li-Zr合金剥蚀性能的影响[J].中南大学学报(自然科学版),2008(04):735-740. |
| [4] | 李红英,曾再得,王娄翔,郑子樵.时效状态对新型Al-Cu-Li系合金剥落腐蚀性能的影响[J].材料热处理学报,2007(06):134-138,147. |
| [5] | 易俊兰,陈磊,陈洁,朱瑞鑫,吴松林,宋袁曾.合金化中主要析出相对铝锂合金局部腐蚀的影响机制研究进展[J].腐蚀与防护,2011(10):822-825,844. |
| [6] | P. Campestrini;E. P. M. van Westing;A. Hovestad;J. H. W. de Wit .Investigation of the chromate conversion coating on alclad 2024 aluminium alloy: effect of the pH of the chromate bath[J].Electrochimica Acta,2002(7):1097-1113. |
| [7] | Devicharan Chidambaram;Clive R. Clayton;Gary P. Halada .The role of hexafluorozirconate in the formation of chromate conversion coatings on aluminum alloys[J].Electrochimica Acta,2006(14):2862-2871. |
| [8] | Varma, PCR;Duffy, B;Cassidy, J .Influence of magnesium nitrate on the corrosion performance of sol-gel coated AA2024-T3 aluminium alloy[J].Surface & Coatings Technology,2009(3):277-284. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%