用慢应变速率拉伸测试、金相(OM)、扫描电镜(SEM)及透射电镜(TEM)分析等方法研究了Al-3.88Cu-1.18Mg-0.31Mn铝合金在T6时效状态下的应力腐蚀开裂(sCC)行为.结果表明:随着时效时间的延长,合金的应力腐蚀开裂敏感性逐渐降低.合金应力腐蚀与晶间腐蚀具有正相关性,其本质是晶界与晶内存在电位差,形成电偶腐蚀,在应力作用下,导致晶界连续腐蚀.在时效过程中,晶界S '(S)相由连续分布逐渐转变为断续分布,晶内析出相由GPB区逐渐转变为S'(S)相,并形成PFZ.这样的微观组织转变使合金应力腐蚀开裂敏感性随着时效的进行逐渐降低.
参考文献
| [1] | T. Warner .Recently-Developed Aluminum Solutions for Aerospace Applications[J].Materials Science Forum,2006(Pt.2):1271-1278. |
| [2] | 刘兵,彭超群,王日初,王小锋,李婷婷.大飞机用铝合金的研究现状及展望[J].中国有色金属学报,2010(09):1705-1715. |
| [3] | 刘继华,朱国伟,李荻,郭宝兰,刘培英.电极极化对铝合金应力腐蚀断裂敏感性的影响[J].材料保护,2005(03):25-27. |
| [4] | 刘继华.高强铝合金的应力腐蚀测试方法综述与评价[J].材料工程,2007(10):76-80. |
| [5] | Chang CH;Lee SL;Lin JC;Yeh MS;Jeng RR .Effect of Ag content and heat treatment on the stress corrosion cracking of Al-4.6Cu-0.3Mg alloy[J].Materials Chemistry and Physics,2005(2/3):454-462. |
| [6] | 陈险峰,彭大暑,张辉,林启权,林高用.热处理制度对2519铝合金板材力学性能和应力腐蚀敏感性的影响[J].中国有色金属学报,2003(04):934-938. |
| [7] | 张新明,李慧中,陈明安,梁霄鹏,李洲,贾寓真.热处理对2519铝合金应力腐蚀开裂敏感性的影响[J].中国有色金属学报,2006(10):1743-1748. |
| [8] | 葛婧萱,郑子樵,罗先甫.热处理制度对2056铝合金微观组织和抗应力腐蚀性能的影响[J].中国有色金属学报,2011(12):2995-3001. |
| [9] | GB/T 15970.7-2000..金属和合金的腐蚀应力腐蚀试验第7部分:慢应变速率试验[S]. |
| [10] | HB 7235-95..慢应变速率应力腐蚀试验方法[S]. |
| [11] | 束德林.工程材料力学性能[M].北京:机械工业出版社,2003:147-153. |
| [12] | 苏景新,张昭,曹发和,张鉴清,曹楚南.铝合金的晶间腐蚀与剥蚀[J].中国腐蚀与防护学报,2005(03):187-192. |
| [13] | Li J F;Zheng Z Q;Jiang N et al.Localized corrosion mechanism of 2xxx-series Al alloy containing S(Al2CuMg) and θ'(Al2Cu) precipitates in 4.0％ NaCl solution at pH 6.1[J].Materials Chemistry and Physics,2005,91(2/3):325-329. |
| [14] | Christine Blanc;Alexandre Freulon;Marie-Christine Lafont;Yolande Kihn;Georges Mankowski .Modelling the corrosion behaviour of Al_2CuMg coarse particles in copper-rich aluminium alloys[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(11):3838-3851. |
| [15] | S.C. Wang;M.I. Starink .The assessment of GPB2/S" structures in Al-Cu-Mg alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):156-163. |
| [16] | 李松瑞;周善初.金属热处理[M].长沙:中南大学出版社,2003:236-238. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%