在深海环境中,海水的压力、温度和含氧量等因素会影响有机涂层的使用寿命.本文研究模拟深海环境对涂层带有人工破损时,涂覆以改性厚浆环氧防锈涂层的907A钢试样在天然海水中的电化学阻抗谱响应特征和涂层耐蚀性能变化.结果表明,在相同破损率和相同浸泡时间条件下,与常压下试样相比,处于2.5 MPa的压力下试样的阻抗幅值显著变小,而且随浸泡时间延长,试样的涂层电容呈增加趋势,极化电阻不断减小,证实了海水压力加速了涂层的失效过程.同时表明,在模拟深海环境中运用电化学交流阻抗对研究有机涂层失效过程是可行的.
参考文献
| [1] | Beaunier L,Epelboin I,Lestrade J C,et al.Etude electrochimique,et par microscopie electronique a balayage,du fer recouvert de peinture[J].Surf.Technol.,1976,4:237. |
| [2] | Kendig M,Mansfeld F,Tsai S.Determination of the long term corrosion behavior of coated steel with A.C.impedance measurements[J].Corrosion,1983,23:317. |
| [3] | Miszczyk A,Darowicki K.Accelerated ageing of organic coating systems by thermal treatment[J].Corrosion,2001,43:1337. |
| [4] | Yong X F,Li J,Croll S G,et al.Degradation of low gloss polyurethane aircraft coatings under UV and prohesion alternating exposures[J].Polym.Degrad.Stab.,2003,80:51. |
| [5] | Touzain S,Thu Q L,Bonnet G.Evaluation of thick organic coatings degradation in seawater using cathodic protection and thermally accelerated tests[J].Prog.Org.Coat,2005,52:311. |
| [6] | 胡吉明,张鉴清,谢德明等.环氧树脂涂覆LY12铝合金在NaCl溶液中的阻抗模型[J].物理化学学报,2003,19:144. |
| [7] | Dehri I,Erbil M.The effect of relative humidity on the atmospheric corrosion of defective organic coating materials:an EIS study with a new approach[J].Corrosion,2000,42:969. |
| [8] | Bajat J B,Miskovic-Staknovic V B.Protective properties of epoxy coatings electrodepesited on steel electrochemically modified by Zn-Ni alloys[J].Prog.Org.Coat,2004,49:183. |
| [9] | 阎瑞,耿志,吴行等.潜艇表面涂层失效机理的研究[J].海军工程大学学报,2005,17(5):38. |
| [10] | 王成,吴航,杨怀玉等.有机涂层在模拟深海环境中的电化学行为的研究[J].腐蚀科学与防护技术,2009,21(4):351. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%