复合脱氧后钢液的最终氧含量优于单独脱氧的效果,同时复合脱氧可产生低熔点、易聚合长大的复合夹杂物,实现最佳的脱氧效果。用热力学方法计算了铝-硅-锰复合脱氧的效果,结果表明,在不同硅锰比下,复合脱氧均比单独用铝脱氧的最终氧含量要低;根据脱氧产物为锰铝榴石的原则得出了合金脱氧剂的组成成分。热态试验验证了理论计算结果。
The final reactive oxygen content in liquid steel by compound deoxidation react which can produce the low melting point and aggregated inclusions is lower than that by aluminum deoxidation react.Compound deoxidation react by Al-Si-Mn alloy was calculated according to thermodynamic principle.The results indicate that the final reactive oxygen content in liquid steel by Al-Si-Mn deoxidation is lower than that by Al deoxidation.The component of deoxidizing alloy is calculated to obtain the spessartite.The calculation result in theory was confirmed by the inclusion composition in steel sample by alloy deoxidation in a SiMo furnace.
参考文献
| [1] | 棍冈博幸;李宏.炉外精炼一一向多品种、高质量钢大生产的挑战[M].北京:冶金工业出版社,1997 |
| [2] | 藤泽敏治;坂尾弘.Mn-Si-Al复合脱酸にぉける溶钢と脱酸生成物との平衡关系[J].铁と钢,1977(09):1494. |
| [3] | 曲英.钢铁学原理[M].北京:冶金工业出版社,1981 |
| [4] | Hiroki Ohta;Hideaki Sut T O .Activities in CaO-SiO2-Al2O3 Slag and Deoxidation Equilibria of Si and Al[J].Metallurgical and Materials Transaetions,1996,27B:943. |
| [5] | Sigworth G K;Elliott J F .The Thermodynamics of Liquid Dilute Iron Alloys[J].Metal Science Journal,1974,18:298. |
| [6] | 黄希祜.钢铁冶金原理[M].北京:冶金工业出版社,2004 |
| [7] | Le T T;Ichikawa M.Optimization of Calcium Treatment at Dofasco[A].Toronto:Canadian Institute of Mining,Metallurgy and Petroleum in Montreal,1994:29. |
| [8] | 德国钢铁工程师协会(西德).渣图集[M].北京:冶金工业出版社,1989 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%