采用非均相成核法,在Sn(OH)4晶种上均匀生长Sb掺杂Sn(OH)4,制备纳米ATO粉末.以电阻测定系统研究了合成条件如掺杂浓度、反应温度、pH值、SnCl4浓度等对最终粉末电阻性能的影响.以TG-DSC热分析、XRD、TEM等手段研究了晶粒生长过程,XRD显示为四方金红石型结构,平均粒径为15nm.当Sb/Sn(mol比)=0.05,pH=2,T=60℃,SnCl4=1.2～1.8mol@L-1时,粉体电阻小于0.5Ω.
参考文献
| [1] | Rockenberger J.;Tischer M.;Troger L.;Haase M.;Weller H.;zum Felde U. .Near edge X-ray absorption fine structure measurements (XANES) and extended x-ray absorption fine structure measurements (EXAFS) of the valence state and coordination of antimony in doped nanocrystalline SnO2[J].The Journal of Chemical Physics,2000(9):4296-4304. |
| [2] | Coleman J P;Freeman J J;Madhukar P et al.[J].Displays,1999,20:145-154. |
| [3] | Paria M L;Smaiti H .[J].Journal of Materials Science,1982,17:3275-3280. |
| [4] | Kembeza E S;Richard V;Van Landuyt J et al.[J].Materials Research Bulletin,1999,34:1527-1533. |
| [5] | 中国科学院数学研究所统计组.常用数理统计方法[M].北京:科学出版社,1973 |
| [6] | Shanti E;Dutta V;Banerjee A .[J].Journal of Applied Physics,1980,51:6243-6280. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%