采用扫描电化学显微镜（SECM）技术,结合电导率和循环伏安测试,研究了304不锈钢在NaCl溶液中的点蚀行为。结果表明,点蚀早期阶段,在不锈钢表面首先产生不稳定的电活性点;点蚀形成的过程中,这些电活性点或消失或成为稳定点蚀坑,并同时出现新的电活性点。电活性点的产生与消失及点蚀的形成是同时发生的。NaCl溶液的电导率与其所含Fe2＋浓度有关,Fe2＋浓度越高,超微电极探针检测到的稳态电流越大。
Pitting corrosion process of 304 stainless steel in NaCl solution was investigated using scanning electrochemical microscopy（SECM）,combined with the measurements of electrical conductivity and cyclic voltammetry.The results showed that there were meta-stable electrically active sites on the surface of stainless steel in the initial pitting process.In the formation process of pits,some initiated meta-stable electrically active sites might disappear,some might propagate and finally become stable pits,while new ones might be induced.The generation,disappearance of meta-stable electrically active sites and formation of pits occurred simultaneously.The electrical conductivity of NaCl solution was related with the concentration of Fe2＋ in the solution.The higher the concentration of Fe2＋ in NaCl solution,the greater the steady-state current detected by superfine electrode probe.
参考文献
| [1] | 任三元,曹定国,王文亮.航空装备腐蚀防护控制技术进展与展望[J].装备环境工程,2008(03):40-45. |
| [2] | 顾彩香,吉桂军,朱冠军,李伟,田晓禹,丁树丹.船舶的腐蚀与防腐措施[J].船舶工程,2010(03):1-4,8. |
| [3] | 王力伟,李晓刚,杜翠薇,曾笑笑.微区电化学测量技术进展及在腐蚀领域的应用[J].中国腐蚀与防护学报,2010(06):498-503,512. |
| [4] | 骆鸿,魏丹,董超芳,肖葵,李晓刚,林春芳.金属腐蚀微区电化学研究进展（1）扫描电化学显微镜技术[J].腐蚀与防护,2009(07):437-441. |
| [5] | Davoodi A;Pan J;Leygraf C;Norgren S .Probing of local dissolution of Al-alloys in chloride solutions by AFM and SECM[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(15):5499-5503. |
| [6] | Q. Yang;J. L. Luo .The hydrogen-enhanced effects of chloride ions on the passivity of type 304 stainless steel[J].Electrochimica Acta,2000(24):3927-3937. |
| [7] | Yuan, Y.;Li, L.;Wang, C.;Zhu, Y. .Study of the effects of hydrogen on the pitting processes of X70 carbon steel with SECM[J].Electrochemistry communications,2010(12):1804-1807. |
| [8] | J. G. Yu;J. L. Luo;P. R. Norton .Investigation of hydrogen induced pitting active sites[J].Electrochimica Acta,2002(25):4019-4025. |
| [9] | J. G. Yu;J. L. Luo;P. R. Norton .Electrochemical investigation of the effects of hydrogen on the stability of the passive film on iron[J].Electrochimica Acta,2002(10):1527-1536. |
| [10] | 曹佳,邵亚薇,张涛,孟国哲.磷酸锌对环氧涂层破损处金属的缓蚀作用[J].中国腐蚀与防护学报,2009(06):437-441. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%