Cemented Carbide YG11C and Tool Steel Crl2MoV was blazed with Ni-base amorphous alloys, QG-1011,MBF-20 and MBF-75, using dynamics thermodynamics analogue testing machine Gleeble 1500D. The effects of brazing temperature, holding time and holding pressure on micro-structure and bond strength were investigated. Results showed that YG11C and Cr12MoV were all wetted well by these three Ni-base alloys, and the bond strength was as high as 220MPa,320MPa, 320MPa respectively. When the blazing temperature was at the point over the melting point 60-70℃ of Ni-base alloy, the holding time was about 2-10min, the suitable pressure was benefit for improving the brazing quality.Microanalysis showed Co in cemented carbide diffused into liquid brazing alloy and formed the Fe-Co solid .solution.
参考文献
| [1] | Zhou Juanfang.[J].机械工程师,1997(09):40-43. |
| [2] | Zhang Qiyun;Zhuang Hongshou.Brazing Book[M].北京:机械工业出版社,1998:300-301,366. |
| [3] | Lin Huiguo;Lin Gang;Wu Jingwen.Handbook of designation and trade name of worldwide steels pocket edition[M].北京:机械工业出版社,2003:4-4,4-23. |
| [4] | YU Jueqi;Yi Wenzhi;Chen Bangdi.Collection of Binary alloy Phase Diagram[M].上海:上海科学技术出版社,1987 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%